常用材料对照表
NO
GB 699
ГОСТASTM/AISI
BS
NF DIN
JIS
108F 08КПUst14
SPH1208081008
040A04050A04
S9CK
310F 10КПUst13
SHP2410101010040A10045A10060A10C10,XC10
C10,CK10
S10C 515F 15КПSHP3
615
15
1015040A15050A15060A15C15,XC15C15,CK15
S15C S15CK 720201020040A20050A20060A20C20,XC18C22,CK22S20C 825251025060A25070M26C25,XC25C25,CK25S25C 930301030060A30C30,XC32C30,CK30S30C 1035351035060A35C35,XC35C35,CK35S35C 1140401040060A40C42,XC42C40,CK40S40C 1245451045060A42060A47C45,XC45C45,CK45S45C 13505010491050060A52C50,XC48C50,CK50S50C 1455551055060A57070M35C55,XC55C55,CK55S55C 1560601060060A62C60,XC60C60,CK60S58C
16656510641065060A67C65,XC65C67,CK6717707010691070060A72070A72C70,XC70C70,CK7018757510741075060A78070A78XC75C75,CK751980801080060A83XC80CK8020858510841085050A86060A86XC85CK852115Mn 15Г1016080A15080A17XC1214Mn415Mn32220Mn 20Г10191022080A20080A22XC18
19Mn520Mn521Mn42325Mn 25Г10251026
080A25080A2726Mn52430Mn 30Г
1033
080A30080M30XC3230Mn431Mn430Mn52535Mn 35Г1037080A35080M3635Mn435Mn52640Mn 40Г1039080A40080M4040M5
40Mn42745Mn 45Г1046080A47080M4646Mn5
2850Mn 50Г10531051080A52080M50XC48
50Mn552Mn52960Mn 60Г10621061080A57080A62CK603065Mn 65Г1566080A6765Mn4
3170Mn 70Г1572080A723220Mn220Г213201321150M1920M520Mn5SMn2133
30Mn2
30Г2
1330
150M28
32M5
30Mn5
SMn24
Metal materials commonly used brand of table
ISO 683/1
C25,C25E4,C25M2C30,C30E4,C30M2C35,C35E4,C35M2C40,C40E4,C40M2C45,C45E4,C45M2C50,C50E4,C50M2C55,C55E4,C55M2C60,C60E4,C60M2
3435Mn235Г21335150M3635M536Mn5SMn1
3540Mn240Г21340
1341
40M5SMn2
3645Mn245Г2134545m546Mn7SMn3 3750Mn250Г2105255M550MNn7
3820MnV20MnV6
3927SiMn27CГ27MnSi5
4035SiMn35CГ38MS537MnSi5
4142SiMn43CГ38MS538MnSi4 46MnSi4
4240B14B3535B2 4345B50B46H45B2 4450B14B50
4540MnB15B4138MB540MB4
4645MnB 15B48 50B44
4715Cr15X 5015
5115
523A14
523M15
12C315Cr3SCr21
4820Cr20X5120527A19
527M20
18C3,18C420Cr4SCr22
4930Cr30X5130530A30
530A32
28C4,32C428Cr4SCr2
5035Cr35X5135530A3638C434Cr4,37Cr4SCr3
5140Cr40X5140530A40
530M40
42C441Cr4SCr4
5245Cr45X514545C442Cr4SCr5
5338CrSi 37XC 38XC
5412CrMo12XM411912CD413CrMo4.4
5515CrMo15XM A-387Cr.B165315CD4.05
15CrMo5
16CrMo4.4
SCM21
5620CrMo20XM4118CDS12,CDS11018CD4,20CD420CrMo5
22CrMo4
SCM22
5730CrMo30XM4130CDS1330CD425CrMo4SCM2
5835CrMo35XM 4135
4137
708A3735CD4
34CrMo4
35CrMo4
SCM3
5942CrMo38XM 4140
4142
708M40
708A42
709M40
40CD4
42CD4
41CrMo4
42CrMo4
SCM4
6012CrMoV12XMΦ
6112Cr1MoV12X1MΦ13CrMoV4.2
6225Cr2Mo1VA25X2M1ΦA
6320CrV20XΦ612022CrV422CrV4
6440CrV40XΦA614042CrV442CrV
6550CrVA50XΦA6150735A5050CV450CrV4SUP10
6615CrMn 15XГ
18XГ
16MC516MnCr5
6720CrMn20XГ5120527A6020MC520MnCr5SMC21 6830CrMnSiA30XГCA
6940CrNi40XH3140640A35
640M40
35NC646NiCr6SNC1
7020CrNi320XH320NC1122NiCr14
7130CrNi330XH3653M3130NC11
30NC12
28NiCr10
31NiCr14
SNC2
7240CrNiMoA40XHMA4340,9810871M40
816M40
35NCD5
40NCD3
36NiCrMo4
40NiCrMo6
SNCM8
731Cr18Ni912X18H9
302
S30200
302S25Z10CN18.09X12CrNi188SUS302
74Y1Cr18Ni9
303
S30300
303S21Z10CNF18.09X12CrNiS188SUS303
750Cr19Ni908X18H10
304
S30400
304S15Z6CN18.09X5CrNi189SUS304
7600Cr19Ni1003X18H11
304L
S30403
304S12Z2CN18.09X2CrNi189SUS304L
770Cr18Ni9Ti08X18H10T
321
S32100
321S12
321S20
Z6CNT18.10X10CrNiTi189SUS321
683/11 20Gr4,20GrS4
683/3 3,3a,3b
683/1 4,4a,4b
683/1 C35ea,C35eb
683/1 3
683/1 4,4a,4b
12
17
11
10
15
780Cr13Al
405
S40500
405S17Z6CA13X7CrAl13SUS405
791Cr1712X17
430
S43000
430S15Z8C17X8Cr17SUS430
800Cr1308X13410S403S17Z6C13X7Cr13SUS410S 811Cr1312X13410410S21Z12C13X10Cr13SUS410
822Cr13
420
S42000
420S37Z20C13X20Cr13SUS420J1
833Cr1330X13420
S45
420S45SUS420J2
847Cr17
440A
S44002
SUS440A
850Cr17Ni7Al09X17H7Ю
631
S17700
Z8CNA17.7X7CrNiAl177SUS631
862Cr23Ni1320X23H12
309
S30900
309S24Z15CN24.13SUH309
872Cr25Ni2020X25H20C2
310
S31000
310S24Z12CN25.20CrNi2520SUH310
880Cr25Ni20
310S
S31008
SUS310S
890Cr17Ni12Mo208X17H13M2T
316
S31600
316S16Z6CND17.12X5CrNiMo1810SUS316
900Cr18Ni11Nb08X18H12E
347
S34700
347S17Z6CNNb18.10X10CrNiNb189SUS347
911Cr13Mo SUS410J1
921Cr17Ni214X17H2
431
S43100
431S29Z15CN16-02X22CrNi17SUS431
930Cr17Ni7Al09X17H7Ю
631
S17700
Z8CNA17.7X7CrNiAl177SUS631
94QT400-18BЧ4060-40-18400/17FGS370-17GGG40FCD400 95QT450-10BЧ4565-45-12420/12FGS400-12FCD450 96QT500-7BЧ5070-50-05500/7FGS500-7GGG50FCD500 97QT600-3BЧ6080-60-03600/7FGS600-2GGG60FCD600 98QT700-2BЧ70100-70-03700/2FGS700-2GGG70FCD700 99QT800-2BЧ80120-90-02800/2FGS800-2GGG80FCD800 100QT900-2BЧ100900/2
101HT100CЧ10100FC100 102HT150CЧ15NO.20150FGL150GG15FC150 103HT200CЧ20NO.30200FGL200GG20FC200 104HT250CЧ25NO.35250FGL250GG25FC250 105HT300CЧ30NO.45300FGL300GG30FC300 106HT350CЧ35NO.50350FGL350GG35FC350 107CЧ40NO.60FGL400GG40
108TU2C10100C101OF-Cu C1011 109T2M1C11000C101E-Cu58C1100 110TP2C12200C106SF-Cu C1220 111TP1C12000SW-Cu C1201 112TAg0.1C10400CuAg0.1C1040 113H90JI90C22000CZ101CuZn10C2200 114H70JI70C26000CZ106CuZn30CuZn30C2600 115H68JI68C26200CuZn33C2620 116H65C27000CZ107CuZn36C2700 117H63JI63C27200CZ108CuZn37C2720 118H62JI62C28000CZ109Cu-Zn40C2800
119QSn4-0.3C51100
C51000PB101
CuSn4
CuSn5
C5111
C5101
120QSn6.5-0.1C51900PB103CuSn6C5191 121QSn8-0.3C52100CuSn8C5210 122QSn6.5-0.4CuSn6P CuNi18Zn20
123BZn18-18C75200NS106CuNi18Zn27C7521 124BZn18-26C77000NS107C7701 125BZn15-20C7541 126BZn18-10C7350 1275A02AMg5052NS45052A1Mg2.55052 1285A03AMg3NS5
Cu-FRHC
2
8
1
3
4
5
683/16 2
20,20a
16
9
683/16 2
400-18
450-10
500-7
600-3
700-2
800-2
900-2
100
150
200
250
300
350
Cu-OF
Cu-DHP
Cu-DLP CuAg0.1
CuZn10
CuZn30
CuZn35
CuZn37
CuZn40
CuSn4
CuSn5
CuSn6
CuSn8 CuNi18Zn20 CuNi18Zn27
1295A05
AMg5V 5056NB6A1Mg5
50561305A305456NG61595755561312A01D1820362117AlCu2.5Mg0.521171322A11D1HF15
2017S AlCuMg120171332A12D16AVTV 21242024
AlCuMg220241342B1623191352A80AK42N011362A90AK2221820181372A14AK820142014AlCuSiMn 20141387A09V95P 71757075
AlZnMgCu1.57075139ZL101A л9A03560A13560LM25A-S7G G-A1Si7Mg AC4C 140ZL102A л2A14130LM20A-S13G-A1Si12AC3A 141ZL104A л4A03600LM9A-S9G A-S10G
G-A1Si10Mg AC4A 142ZL105A л5A03550C33550LM16G-A1Si5Cu AC4D 143ZL106A л14B A03280A03281LM-24G-A1Si8Cu3AC4B 144ZL107A л6/A л74
A03190A03191LM4LM21A-S5UZ A-S903G-A1Si6Cu4
AC2B
145ZL108SC122A LM2146ZL109A л30A03360A03361LM13A-S12UNG AC8A
147ZL110A л10B LM1
G-A1Si(Cu)
148ZL111A л4M A03540A03540
149ZL201A л19A-U5GT
G-A1Cu4TiMg 150ZL202A л12A03600A-U8S 151ZL203A л17A02950A-U5GT
G-A1Cu4Ti 152ZL301A л8A05200A05202LM10LM5G-A1Mg10AC7B 153ZL302A л22A05140A05141L74
A-G6A-G3T G-A1Mg5
AC7A
154ZL401A лP1155ZL402A л24
A07120A07122A-Z5G
156Y102S12A LM6-M
GD-A1Si12ADC1157Y104SG100A
GD-A1Si10Mg
ADC3
158T108159Y112160Y302G4A LM5-M A-G3T GD-A1Mg5161
Y401
GB
C
Si
Mn
P
S
Ni
Cr
Cu
others
08F 0.05-0.11≤0.030.25-0.50≤0.0350.0350.250.10.25080.05-0.120.17-0.370.35-0.65≤0.0350.0350.250.10.2510F 0.04-0.14≤0.070.25-0.50≤0.0350.0350.250.150.25100.07-0.140.17-0.370.35-0.65≤0.0350.0350.250.150.2515F 0.12-0.19≤0.070.25-0.50≤0.0350.0350.250.250.25150.12-0.190.17-0.370.35-0.65≤0.035≤0.035≤0.25≤0.25≤0.25200.17-0.240.17-0.370.35-0.65≤0.035≤0.035≤0.25≤0.25≤0.25250.22-0.300.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25300.27-0.350.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25350.32-0.400.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25400.37-0.450.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25450.42-0.500.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.2550
0.47-0.50
0.17-0.37
0.50-0.80
≤0.035
≤0.035
≤0.25
≤0.25
≤0.25
Steel alloy Chemical Composition
A1Si7Mg A1-Si12A1Si9Mg A1Si10Mg
A1-Si12Cu
A1-Cu4MgTi A1-Si8Cu A1-Cu4MgTi
A1-Mg6A1-Mg3A1-Zn5Mg
A1-Si12Fe
A1-Si3Fe
550.52-0.600.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
600.57-0.650.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
650.62-0.700.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
700.67-0.750.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
750.72-0.800.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
800.77-0.850.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
850.82-0.900.17-0.370.50-0.80≤0.035≤0.035≤0.25≤0.25≤0.25
15Mn0.12-0.190.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
20Mn0.17-0.240.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
25Mn0.22-0.300.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
30Mn0.27-0.350.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
35Mn0.32-0.400.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
40Mn0.37-0.450.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
45Mn0.42-0.500.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
50Mn0.48-0.560.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
60Mn0.57-0.650.17-0.370.70-1.00≤0.035≤0.035≤0.25≤0.25≤0.25
65Mn0.62-0.700.17-0.370.90-1.20≤0.035≤0.035≤0.25≤0.25≤0.25
70Mn0.67-0.750.17-0.370.90-1.20≤0.035≤0.035≤0.25≤0.25≤0.25
20Mn20.17-0.240.17-0.37 1.40-1.80
30Mn20.27-0.340.17-0.37 1.40-1.80
35Mn20.32-0.390.17-0.37 1.40-1.80
40Mn20.37-0.440.17-0.37 1.40-1.80
45Mn20.42-0.490.17-0.37 1.40-1.80
50Mn20.47-0.550.17-0.37 1.40-1.80
20MnV0.17-0.240.17-0.37 1.30-1.60V 0.07～0.12 27SiMn0.24-0.320.17-0.37 1.10-1.40
35SiMn0.32-0.400.17-0.37 1.10-1.40
42SiMn0.39-0.450.17-0.37 1.10-1.40
40B0.37-0.440.17-0.370.60-0.90 B 0.0005-0.0035 45B0.42-0.490.17-0.370.60-0.90 B 0.0005-0.0035 50B0.47-0.550.17-0.370.60-0.90 B 0.0005-0.0035 40MnB0.37-0.440.17-0.37 1.10-1.40 B 0.0005-0.0035 45MnB0.42-0.490.17-0.37 1.10-1.40 B 0.0005-0.0035 15Cr0.12-0.180.17-0.370.40-0.700.70-1.00
20Cr0.18-0.240.17-0.370.50-0.800.70-1.00
30Cr0.27-0.340.17-0.370.50-0.800.80-1.00
35Cr0.32-0.390.17-0.370.50-0.800.80-1.00
40Cr0.37-0.440.17-0.370.50-0.800.80-1.00
45Cr0.42-0.490.17-0.370.50-0.800.80-1.00
38CrSi0.35-0.430.17-0.370.30-0.60 1.30-1.60
12CrMo0.08-0.150.17-0.370.40-0.700.40-0.70Mo 0.40-0.55 15CrMo0.12-0.180.17-0.370.40-0.700.80-1.10Mo 0.40-0.55 20CrMo0.17-0.240.17-0.370.40-0.700.80-1.10Mo 0.15-0.25 30CrMo0.26-0.340.17-0.370.40-0.700.80-1.10Mo 0.15-0.25 35CrMo0.32-0.400.17-0.370.40-0.700.80-1.10Mo 0.15-0.25 40CrMo0.38-0.450.17-0.370.50-0.800.90-1.20Mo 0.15-0.25
12CrMoV0.08-0.15
0.17-0.370.40-0.700.30-0.60Mo0.25-0.35 V0.15-0.30
12Cr1MoV0.08-0.15
0.17-0.370.40-0.700.90-1.20Mo0.25-0.35 V0.15-0.30
25Cr2Mo1VA0.22-0.29
0.17-0.370.50-0.80 2.1-2.50Mo0.90-1.10 V0.30-0.50
20CrV0.17-0.37
40CrV0.37-0.440.17-0.370.50-0.800.80-1.10V 0.10～0.20 50CrVA0.47-0.540.17-0.370.50-0.800.80-1.10V 0.10～0.20 15CrMn0.12-0.180.17-0.37 1.10-1.400.40-0.70
20CrMn0.17-0.230.17-0.370.90-1.200.90-1.20
30CrMnSiA0.27-0.340.90-1.200.80-1.100.80-1.10
40CrNi0.37-0.440.17-0.370.50-0.80 1.00-1.400.45-0.75
20CrNi30.17-0.440.17-0.370.30-0.60 2.75-3.150.60-0.90
30CrNi30.27-0.330.17-0.370.30-0.60 2.75-3.150.60-0.90
40CrNiMoA0.37-0.440.17-0.370.50-0.80 1.25-1.650.60-0.90 Mo 0.15～0.25
1Cr18Ni9
≤0.15≤1.00
≤2.00≤0.035≤0.0308.00-10.0017.00-19.00Y1Cr18Ni9≤0.15≤1.00≤2.00≤0.20≤0.158.00-10.0017.00-19.000Cr19Ni9≤0.07≤1.00≤2.00≤0.035≤0.0308.00-11.0017.00-19.0000Cr19Ni10≤0.030≤1.00≤2.00≤0.035≤0.0308.00-12.0018.00-20.000Cr18Ni9Ti ≤0.08≤1.00≤2.00≤0.035≤0.0309.00-12.00
17.00-19.000Cr13Al ≤0.08≤1.00≤1.00≤0.035≤0.03011.50-14.50Al 0.10～0.30
1Cr17≤0.12≤0.75≤1.00≤0.035≤0.03016.00-18.000Cr13≤0.08≤1.00≤1.00≤0.035≤0.03011.50-13.001Cr13≤0.15≤1.00≤1.00≤0.035≤0.03011.50-13.002Cr130.16～0.25≤1.00≤1.00≤0.035≤0.03012.00-14.003Cr130.26～0.35≤1.00≤1.00≤0.035≤0.03012.00-14.007Cr170.60～0.75≤1.00≤1.00≤0.035≤0.03016.00-18.000Cr17Ni7Al ≤0.09≤1.00≤1.00≤0.035≤0.030 6.50-7.7516.00-18.00≤0.50Al 0.75～1.50
2Cr23Ni13≤0.20≤1.00≤2.00≤0.035≤0.03012.00-15.0022.00-24.002Cr25Ni20≤0.25≤1.50≤2.00≤0.035≤0.03019.00-22.0024.00-26.000Cr25Ni20≤0.08≤1.50≤2.00≤0.035≤0.03019.00-22.0024.00-26.000Cr17Ni12Mo2≤0.08≤1.00≤2.00≤0.035≤0.03010.00-14.0016.00-18.00Mo 2.00～3.00
0Cr18Ni11Nb ≤0.08≤1.00≤2.00≤0.035≤0.0309.00-13.0017.00-19.001Cr13Mo 0.08～0.18≤0.60≤1.00≤0.035≤0.03011.50-14.001Cr17Ni20.11～0.17≤0.80≤0.80≤0.035≤0.030 1.50-2.5016.00-18.000Cr17Ni7Al ≤0.09≤1.00≤1.00≤0.035≤0.030
6.50-
7.50
16.00-18.00
≤0.50Al 0.75～1.50
GB
Fe
Pb
Mn Sn
Al Ni
Zn
Cu
TU20.0040.0040.002
0.002
0.003
99.95T20.005
0.005
99.90TP299.9TP199.90TAg0.10.050.010.05
0.299.5H900.10.030.588.0-91.0H700.10.030.568.5-71.5H680.10.030.567.0-70.0H650.10.030.563.5-68.0H630.150.080.562.0-65.0H620.150.080.560.5-63.5QSn4-0.30.100.05 3.5-4.90.20.3others QSn6.5-0.10.05 6.0-7.00.0020.20.3others QSn8-0.30.10.057.0-9.00.20.2others QSn6.5-0.40.02 6.0-7.0
0.002
0.20.3
others BZn18-180.250.050.516.5-19.563.5-66.5BZn18-260.250.050.516.5-19.553.5-56.5BZn15-200.5
0.02
0.3
13.5-16.5
others
BZn18-10
GB
Si
Cu
Mg
Zn
Mn
Ti Fe
Ni other
5A020.4 1.1 2.0-2.80.15-0.400.45A030.50-0.80
0.1 3.2-3.80.20.30-0.600.55A050.50.1 4.8-5.50.20.30-0.600.55A300.40.1 4.7-5.50.250.05-1.00.42A010.5 2.2-3.00.20-0.500.100.20.52A110.7 3.8-4.80.300.4-0.80.70.1
2A120.5 3.8-4.5 1.2-1.60.100.30-0.700.52B160.25 5.8-6.80.050.20-0.40
0.32A800.50-1.2 1.9-2.5 1.4-1.80.300.2 1.0-1.600.9-1.52A900.50-1.0 3.5-4.50.40-0.80.300.20.50-1.0 1.8-2.32A140.6-1.2 3.9-4.80.4-0.80.300.4-1.00.70.1
7A090.5 1.2-2.0
2.0-
3.0 5.1-6.1
0.15
0.5
Cr 0.16-0.30
ZL101
6.5-
7.5
0.25-0.45
Aluminum alloy Chemical Composition
Copper alloy Chemical Composition
ZL10210.0-13.0
ZL1048.0-10.50.17-0.30.2-0.5
ZL105 4.5-5.5 1.0-1.50.4-0.6
ZL1067.5-8.5 1.0-1.50.3-0.50.3-0.50.10-0.25
ZL107 6.5-7.5 3.5-4.5
ZL10811.0-13.0 1.0-2.00.4-1.00.3-0.9
ZL10911.0-13.00.5-1.50.8-1.30.8-1.5 ZL110 4.0-6.0 5.0-8.00.2-0.5
ZL1118.0-10.0 1.3-1.80.4-0.60.10-0.350.10-0.35
ZL201 4.5-5.30.6-1.00.15-0.35
ZL202
ZL203 4.0-5.0
ZL3019.5-11.0
ZL302
ZL401 6.0-8.00.1-0.39.0-13.0
ZL4020.5-0.65 5.0-6.50.15-0.250.4-0.6
YLD10210.0-13.00.9
YLD1048.0-10.50.2-0.350.2-0.50.8
YLD1127.5-9.5 2.5-4.00.90.2 YLD11716.0-18.0 4.0-5.00.5-0.650.90.3 YLD3020.8-1.3 4.6-5.50.1-0.40.9
YLD306 2.6-4.00.4-0.60.60.1
常用金属材料密度表
材料名称密度(克/厘米3) 灰口铸铁6.6~7.4 白口铸铁7.4~7.7 可锻铸铁7.2~7.4 铸钢7.8 工业纯铁7.87 普通碳素钢7.85 优质碳素钢7.85 碳素工具钢7.85 易切钢7.85 锰钢7.81 15CrA铬钢7.74 20Cr、30Cr、40Cr铬钢7.82 38CrA铬钢7.8 铬钒、铬镍、铬镍钼、铬锰、硅、铬锰硅镍、硅锰、硅铬钢7.85 铬镍钨钢7.8 铬钼铝钢7.65 含钨9高速工具钢8.3 含钨18高速工具钢8.7 高强度合金钢7.82 轴承钢7.81 不锈钢 0Cr13、1Cr13、2Cr13、3Cr13、4Cr13、 Cr17Ni2、Cr18、9Cr18、Cr25、Cr28 7.75 0Cr18Ni9、1Cr18Ni9、Cr18Ni9Ti、2Cr18Ni9 Cr14、Cr17 7.7 4-0.3、4-4-4锡青铜8.9 1Cr18Ni11Si4A1Ti 7.52 7铝青铜7.8 19-2铝青铜 9-4、10-3-1.5铝青铜7.5 9-4、10-3-1.5铝青铜7.5 10-4-4铝青铜7.46 铍青铜8.3 3-1硅青铜8.47 1-3硅青铜8.6 1铍青铜8.8 0.5镉青铜8.9 0.5铬青铜8.9 1.5锰青铜8.8 5锰青铜8.6 白铜B5、B19、B30、BMn40-1.5 8.9 BMn3-12 8.4 BZN15-20 8.6 BA16-1.5 8.7 BA113-3 8.5 纯铝2.7 防锈铝LF2、LF43 2.68
LF3 2.67 LF5、LF10、LF11 2.65 LF6 2.64 LF21 2.73 硬铝LY1、LY2、LY4、LY6 2.76 LY3 2.73 LY7、LY8、LY10、LY11、LY14 2.8 LY9、LY12 2.78 LY16、LY17 2.84 锻铝LD2、LD30 2.7 LD4 2.7 灰铸铁HT100～HT350 6.6--7.4 白口铸铁S15、P08、J13等7.4--7.7 可锻铸铁KT30-6～KT270-2 7.2--7.4 铸钢ZG45、ZG35CrMnSi等7.8 工业纯铁DT1--DT6 7.87 普通碳素钢Q195、Q215、Q235、Q255、Q275 7.85 优质碳素钢05F、08F、15F 10、15、20、25、30、35、40、45、50 7.85 碳素工具钢T7、T8、T9、T10、T12、T13、T7A、T8A、T9A、T10A、T11A、T12A、T13A、T8MnA 7.85 易切钢Y12、Y30 7.85 弹簧钢丝Ⅰ、Ⅱ、Ⅱa、Ⅲ7.85 低碳优质钢丝Zd、Zg 7.85 锰钢20Mn、60Mn、65Mn 7.81 铬钢15CrA 20Cr、30Cr、40Cr 38CrA 7.74 7.82 7.80 铬钒钢50CrVA 7.85 铬镍钢12CrNi3A、20CrNi3A 37CrNi3A 7.85 铬镍钼钢40CrNiMoA 7.85 铬镍钨钢18Cr2Ni4WA 7.8 铬钼铝钢38CrMoA1A 7.65 铬锰硅钢30CrMnSiA 7.85 铬锰硅镍钢30CrMnSiNi2A 7.85 硅锰钢60Si2nMnA 7.85 硅铬钢70Si2CrA 7.85 高强度合金钢GC-4、GC11 7.82 高速工具钢W9Cr4V W18Cr4V 8.3 8.7 轴承钢GCr15 7.81 不锈钢0Cr13、1Cr13、2Cr13、3Cr13、4Cr13 Cr14、Cr17 Cr17Ni2、Cr18、9Cr18、Cr25、Cr28 0Cr18Ni9、1Cr18Ni9 1Cr18Ni9Ti、2Cr18Ni9 Cr18Ni11Nb 1Cr23Ni18、Cr17Ni3Mo2Ti 1Cr18Ni11Si4A1Ti
中德金属材料对照表_2007
Comparison of German and Chinese material designations, Basic SN359 No guarantee in respect of completeness and substitution of materials!ATE2 Standardisiation department kuwe@https://www.wendangku.net/doc/0812113945.html, Material designation Basis SN359Material No. Former designation Standard Remark Material designation Standard Title Remark Matching of properties: E295 1. 0050St 50-2DIN EN 10025-2 -Q275 Z GB 700-88Unalloyed engineering steels C content 0.28 to 0.38%, only limited weldability, Z = Fully killed steel only is permissible,identical E335 1. 0060St 60-2DIN EN 10025-2 -Q 345 A GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible identical E360 1. 0070St 70-2DIN EN 10025-2 -Q 390 A GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible identical S235JR 1. 0038St 37-2 R St 37-2 S235JRG2DIN EN 10025-2KV at room temperature, unkilled not permitted Q 235 B GB 700-88 Unalloyed engineering steels Fully killed steel is permissible identical S235J0 1. 0114R St 37-3 S235J0G2DIN EN 10025-2KV at 0°C, unkilled not permitted Q 235 C GB 700-88Unalloyed engineering steels Fully killed steel only permissible, KV at 0°C ,similar S235J2 1. 0117Q St 37-3N S235J2G3DIN EN 10025-2KV at -20°C, unkilled not permitted Q 235 D GB 700-88Unalloyed engineering steels Fully killed or double-killed steel is permissible, KV at -20°C ,similar S275JR 1. 0044St 44-2 S275JRG2 S275JRC DIN EN 10025-2KV at room temperature, unkilled not permitted Q 275 Z GB 700-88Unalloyed engineering steels C content must be limited to 0.22%, otherwise only limited weldability, notch impact energy not guaranteed.similar Q 275 GB 700-88Unalloyed engineering steels C content must be limited to 0.22%, notch impact energy not guaranteed.do not use Q 345 C GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at 0°C, similar Q 275GB 700-88Unalloyed engineering steels C content must be limited to 0.22%, notch impact energy not guaranteed. do not use Q 345 D GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at -20°C., identical S355JR 1. 0045 -DIN EN 10025-2KV at room temperature, unkilled not permitted Q 345 B GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, identical S355J0 1. 0553S355J0G2DIN EN 10025-2KV at 0°C, unkilled not permitted Q 345 C GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at room 0°C,identical S355J2 1. 0569S355J2G3DIN EN 10025-2KV at -20°C, unkilled not permitted Q 345 D GB T 1591-94High strength low alloy structural steels Fully killed steel is permissible, KV at -20°C.,identical S355N 1. 0545StE 355DIN EN 10025-3normalised, KV at -20°C,Q 345 D GB T 1591-94High strength low alloy structural steels KV at -20°C similar S355NL 1. 0546TStE 355DIN EN 10025-3normalised KV at -50°C,Q 345 E GB T 1591-94High strength low alloy structural steels KV at -40°C !similar S420N 1. 8902StE 420DIN EN 10025-3normalised KV at -20°C,Q 420 D GB T 1591-94High strength low alloy structural steels KV at -20°C !similar S420NL 1. 8912TStE 420DIN EN 10025-3normalised KV at -50°C,Q 420 E GB T 1591-94High strength low alloy structural steels KV at -40°C !similar S460N 1. 8901StE 460DIN EN 10025-3normalised KV at -20°C,Q 460 D GB T 1591-94High strength low alloy structural steels KV at -20°C !similar S460NL 1. 8903TStE 460DIN EN 10025-3normalised KV at -50°C,Q 460 E GB T 1591-94High strength low alloy structural steels KV at -40°C !similar German Chinese Engineering steels Fine-grained engineering steels, weldable DIN EN 10025-2Status: 01.05.2007 in progress KV at 0°C, unkilled not permitted S275J2 1. 0145St 44-3N S275J2G3 S275J2G3C S275J2G4DIN EN 10025-2KV at -20°C, unkilled not permitted S275J0 1. 0143St 44-3
中外金属材料对照表
常用国内外钢材牌号对照表 中国 美国 日本 德国 英国 法国 前苏联 国际标准化组织 GB AST JIS DIN 、DINEN BS 、BSEN NF 、NFEN ΓOCT ISO 630 品 名 牌号 牌号 牌号 牌号 牌号 牌号 牌号 Q195 Cr.B Cr.C SS330 SPHC SPHD S185 040 A10 S185 S185 CT1K П CTlC П CTl ПC Q215A Cr.C Cr.58 SS 330 SPHC 040 A12 CT2K П—2 CT2C П—2 CT2ПC —2 Q235A Cr.D SS400 SM400A 080A15 CT3K П—2 CT3C П—2 CT3ПC —2 E235B Q235B Cr.D SS400 SM400A S235JR S235JRGl S235JRG2 S235JR S235JRGl S235JRG2 S235JR S235JRGl S235JRG2 CT3K П—3 CT3C П—3 CT3ПC —3 E235B Q255A SS400 SM400A CT4K П—2 CT4C П—2 CT4ПC —2 普 通 碳 素 结 构 钢 Q275 SS490 CT5C П—2 CT5ПC —2 E275A
中国 美国 日本 德国 英国 法国 前苏联 国际标准化组织 GB AST JIS DIN 、DINEN BS 、BSEN NF 、NFEN ΓOCT IS0 630 品 名 牌号 牌号 牌号 牌号 牌号 牌号 牌号 08F 1008 1010 SPHD SPHE 040A10 80K П 10 1010 S10C S12C CKl0 040A12 XCl0 10 C101 15 1015 S15C S17C CKl5 Fe360B 08M15 XCl2 Fe306B 15 C15E4 20 1020 S20C S22C C22 IC22 C22 20 25 1025 S25C S28C C25 IC25 C25 25 C25E4 40 1040 S40C S43C C40 IC40 080M40 C40 40 C40E4 45 1045 S45C S48C C45 IC45 080A47 C45 45 C45E4 50 1050 S50C S53C C50 IC50 080M50 C50 50 C50E4 优 质 碳 素 结 构 钢 15Mn 1019 080A15 15r
常用国内外材料的标准及牌号对照
一. 常用国内外紧固件材料的标准及牌号对照 表<-> 钢中国GB 美国ASTM 德国DIN 日本工业JIS 英国BS 种标准种类代号标准种类代号标准种类代号牌号标准种类代号标准种类代号A194 Gr.1 Gr.2 GB669 45 Gr.2H G4051 S43C 4882 Gr.2H S45C Gr.2HM GB669 35 A307 Gr.A G3101 SS4l 5708 SS41 碳 素GB669 20 Gr．B G4051 S20C 1769 钢GB669 25 S25C GB669 30 A325 1 型1654 Cq85 1.1172 CG4051 S33C 8189 2 型 3A型 3B型 3C型 3D型 3E型 3F 型 YB6 1Cr5Mo A193 Gr．B5 G4107 SNB5 Gr．B6 GBl220 1Crl3 Gr．B6X 17440 X15Crl3 1.4024 4882 Gr．B6 GB307735CrMOA A193 Gr．B7 17200 42CrMo4 1.7225 G4107 SNB7 4882 Gr．B7 合 金 Gr．B7M 钢 和 YB6 15CrM01V Gr．B16 17240 21CrMoV57 1.7709 SNBl6 Gr．B16 不 GBl220 0Crl8Ni9 GL B8 17440 X5CrNi189 1.4301 G4303 SUS-304 GL.B8 锈 钢 Gr．B8A GBl220 1Crl8NillNb Gr．B8C X10CrNiNbl89 1.4550 SUS-347 Gr.B8C Gr．B8CA GBl220 0C17Nil2M02 Gr．B8M X5CrNiMo1810 l.4401 SUS-316 Gr.B8M Gr．B8MA Gr．B8N Gr.B8NA
中德材料对照表1
中德常用金属材料对照表Comparison List For Standard Material 一、普通碳素结构钢Carbon structure steel Page 1 of 15 *Remark:20MnMo will be used for forged material
一、碳素结构钢Carbon structure steel Page 2 of 15 （a）V：调质处理quenching and tempering； （b）①为调质处理时参数parameter after quenching and tempering。
一、碳素结构钢Carbon structure steel Page 3 of 15 注：N：正火。 Note:N-normalizing
二、合金结构钢Alloy structure steel Page 4 of 15 Note： ① For section ≤100,QT；② When section≤ 120，QT；③When section is 15，QT；④ When section is 25，QT；⑤ When section is 30，QT。* If the bill of material(b.o.m) will not request the “V”(quench and temper) the material will be converted without the +QT by CMMP If the material “+QT” will not be available, CMMP will do the quenching and tempering to reach the requested material properties.
钢材表-中德对照表
摘要:钢材表-中德对照表 优质碳素结构钢 中国德国材料分组 Y15 10S20(1.0721) 抗拉强度〈700MPa Y20 22S20(1.0724) 抗拉强度〈700MPa Y30 35S20(1.0726) 抗拉强度〈700MPa 优质碳素结构钢 中国德国材料分组 10 CK10(1.1121) 抗拉强度〈700MPa 15 C15(1.0401),CK15(1.1141),Cm15(1.1140) 抗拉强度〈700MPa 35 C35(1.0501),CK35(1.1181),Cm35(1.1180) 抗拉强度〈700MPa 45 C45(1.0503),CK45(1.1191),Cm45(1.1201) 抗拉强度700MPa~1000MPa 55 C55(1.0535),CK55(1.1181),Cm55(1.1209) 抗拉强度700MPa~1000MPa 60 C60(1.0601),CK60(1.1221),Cm60(1.1223) 抗拉强度700MPa~1000MPa 15Mn 17Mn4(1.8044) 抗拉强度〈700MPa 40Mn 40Mn4(1.5038) 抗拉强度700MPa~1000MPa 合金结构钢 中国德国材料分组 30Mn2 28Mn6(1.5065),30Mn5(1.5066) 抗拉强度〈700MPa 35Mn2 36Mn5(1.5067) 抗拉强度〈700MPa 35SiMn 37MnSi5(1.5122) 42SiMn 46MnSi4(1.5121) 15MnV 15MnV5(1.5213) 42Mn2V 42MnVT(1.5223) 35Cr 34Cr4(1.7033),37Cr4(1.7034) 抗拉强度700MPa~1000MPa 40Cr 41Cr4(1.7035) 抗拉强度1000MPa~1300MPa 15CrMn 20MnCr4(1.7147) 抗拉强度700MPa~1000MPa 20CrV 22CrV4(1.7513) 40CrV 42CrV6(1.7561) 50CrV 50CrV4(1.8159) 抗拉强度1000MPa~1300MPa 16Mo 15Mo3(1.5415) 抗拉强度〈700MPa 12CrMo 13CrMo44(1.7335) 抗拉强度〈700MPa 15CrMo 16CrMo44(1.7337) 抗拉强度700MPa~1000MPa 20CrMo 25CrMo4(1.7218) 抗拉强度700MPa~1000MPa 30CrMo 34CrMo4(1.7220) 抗拉强度1000MPa~1300MPa 35CrMo 34CrMo4(1.7220) 抗拉强度1000MPa~1300MPa 42CrMo 42CrMo4(1.7225) 抗拉强度1000MPa~1300MPa 38CrMoAl 34CrAlMo5(1.8507) 抗拉强度700MPa~1000MPa 15CrMnMo 15CrMo5(1.7262) 抗拉强度700MPa~1000MPa 20CrMnMo 20CrMo5(1.7264) 抗拉强度700MPa~1000MPa 24CrMoV 24CrMoV55(1.7733) 12CrNi3A 14NiCr10(1.5732) 抗拉强度〈700MPa
各国常用材料牌号对照表
材料类型应用 承 (内 )压铸件铸铁 一般铸件 承 (内 )压铸件 轧材 /锻件 棒材 :承(内) 压 棒材 :一般碳钢 螺栓和螺柱 螺母 板材 管材 各国常用材料牌号对照表 材料牌号 中国德国美国 GB DIN ASTM UNS HT2500.6025GG-25 A 278 Class 3.0 F 12401 HT3000.6030GG-30 A 48 Class25/30 F 11701/F 12101 ZG230-450 1.1155GS-Ck25 A 216 Gr LC8J 03 003 Q235 1.0402C22A266 Class2K 03506 Q235 1.0402C22 A 295 Gr D40G 10 200 45 1.0503C45A576 Gr 1045G10 450 30CrMo 1.725824CrMo5 A 193 Gr B7G41 400 35 1.1181CK35 A 194 Gr 2H K 04 002 Q255 1.0254St.37.0 A 516 Gr 65/70K 02 403/K 02 700 20Mn 1.0305St.35.8 A 106 Gr B K 03 006
材料类型AISI410 钢12%铬钢 材料牌号 应用中国德国美国 GB DIN ASTM UNS 配件20 1.0308St35.0 A 105K 03 504棒料42CrMo 1.722542CrMo4 A 434 Class BB G 41 400 c 螺栓和螺柱35CrMoV 1.771140CrMoV47 A 193 GrB7G 41 400螺母30CrMo 1.725824CrMo5 A 194 Gr 2H K 04 002 ZG1Cr13 1.4008G-X8CrNi13 A 217 Gr CA 15J 91 150承 (内 )压铸件 1.4313G-X5Ni13 4 A 487 Gr CA6NM J 91 540 轧材 /锻件 : 1Cr13 1.4006X10Cr13 A 182 Gr F6a Class1S 41 000 承(内)压 1.4313X4CrNi13 4 A 182 Gr F6NM S 41 500轧材 /锻件 :一般 1.4313X4CrNi13 4 A 473 Type 410S 41 000棒料 : 承(内 )压1Cr13 1.4006X10Cr13 A 479 Type 410S 41 000棒料 :一般 A 276 Type 410S 41 000
金属材料硬度对照表
一、硬度简介： 硬度表示材料抵抗硬物体压入其表面的能力。它是金属材料的重要性能指标之一。一般硬度越高，耐磨性越好。常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。 1.布氏硬度(HB) 以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。 2.洛氏硬度(HR) 当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的标度来表示： ?HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。 ?HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。 ?HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。 3 维氏硬度(HV) 以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除 以载荷值，即为维氏硬度HV值(kgf/mm2)。 ############################################################################################# 注： 洛氏硬度中HRA、HRB、HRC等中的A、B、C为三种不同的标准，称为标尺A、标尺B、标尺C。 洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N(合10kgf)，最后根据压痕深度计算硬度值。标尺A使用的是球锥菱形压头，然后加压至588.4N(合60kgf)；标尺B使用的是直径为1.588mm(1/16英寸)的钢球作为压头，然后加压至980.7N(合100kgf)；而标尺C使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N(合150kgf)。因此标尺B适用相对较软的材料，而标尺C适用较硬的材料。实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。但各种材料的换算关系并不一致。本站《硬度对照表》一文对钢的不同硬度值的换算给出了表格，请查阅。 ##############################################################################################
常用金属材料密度表
材料名称密度(克/厘米3) 灰口铸铁~ 白口铸铁~ 可锻铸铁~ 铸钢 工业纯铁 普通碳素钢 优质碳素钢 碳素工具钢 易切钢 锰钢 15CrA铬钢 20Cr、30Cr、40Cr铬钢 38CrA铬钢 铬钒、铬镍、铬镍钼、铬锰、硅、铬锰硅镍、硅锰、硅铬钢铬镍钨钢 铬钼铝钢 含钨9高速工具钢 含钨18高速工具钢 高强度合金钢 轴承钢 不锈钢 0Cr13、1Cr13、2Cr13、3Cr13、4Cr13、 Cr17Ni2、Cr18、9Cr18、Cr25、Cr28 0Cr18Ni9、1Cr18Ni9、Cr18Ni9Ti、2Cr18Ni9 Cr14、Cr17 、4-4-4锡青铜 1Cr18Ni11Si4A1Ti 7铝青铜 19-2铝青铜 9-4、铝青铜 9-4、铝青铜 10-4-4铝青铜 铍青铜 3-1硅青铜 1-3硅青铜 1铍青铜 镉青铜 铬青铜 锰青铜 5锰青铜 白铜B5、B19、B30、 BMn3-12 BZN15-20 BA113-3 纯铝 防锈铝LF2、LF43 LF3 LF5、LF10、LF11 LF6 LF21 硬铝LY1、LY2、LY4、LY6
LY3 LY7、LY8、LY10、LY11、LY14 LY9、LY12 LY16、LY17 锻铝LD2、LD30 LD4 灰铸铁HT100～HT350 白口铸铁S15、P08、J13等 可锻铸铁KT30-6～KT270-2 铸钢ZG45、ZG35CrMnSi等 工业纯铁DT1--DT6 普通碳素钢Q195、Q215、Q235、Q255、Q275 优质碳素钢05F、08F、15F 10、15、20、25、30、35、40、45、50 碳素工具钢T7、T8、T9、T10、T12、T13、T7A、T8A、T9A、T10A、T11A、T12A、T13A、T8MnA 易切钢Y12、Y30 弹簧钢丝Ⅰ、Ⅱ、Ⅱa、Ⅲ 低碳优质钢丝Zd、Zg 锰钢20Mn、60Mn、65Mn 铬钢15CrA 20Cr、30Cr、40Cr 38CrA 铬钒钢50CrVA 铬镍钢12CrNi3A、20CrNi3A 37CrNi3A 铬镍钼钢40CrNiMoA 铬镍钨钢18Cr2Ni4WA 铬钼铝钢38CrMoA1A 铬锰硅钢30CrMnSiA 铬锰硅镍钢30CrMnSiNi2A 硅锰钢60Si2nMnA 硅铬钢70Si2CrA 高强度合金钢GC-4、GC11 高速工具钢W9Cr4V W18Cr4V 轴承钢GCr15 不锈钢0Cr13、1Cr13、2Cr13、3Cr13、4Cr13 Cr14、Cr17 Cr17Ni2、Cr18、9Cr18、Cr25、Cr28 0Cr18Ni9、1Cr18Ni9 1Cr18Ni9Ti、2Cr18Ni9 Cr18Ni11Nb 1Cr23Ni18、Cr17Ni3Mo2Ti 1Cr18Ni11Si4A1Ti 2Cr13Ni4Mn9 3Cr13Ni7Si2
金属硬度对照表
硬度对照表 硬度表示材料抵抗硬物体压入其表面的能力。它是金属材料的重要性能指标之一。一般硬度越高，耐磨性越好。常用的 硬度指标有布氏硬度、洛氏硬度和维氏硬度。 1. 布氏硬度（ HB ） 以一定的载荷 ( 一般 3000kg ) 把一定大小（直径一般为 10mm ）的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值 (HB) ，单位为公斤力 /mm2 (N/mm2) 。 2. 洛氏硬度（ HR ） 当 HB>450 或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120 °的金刚石圆锥体或直径为 1.59 、 3 .18mm 的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的甓壤幢硎荆 HRA ：是采用 60kg 载荷和钻石锥压入器求得的硬度，用于硬度极高的材料 （如硬质合金等）。 HRB ：是采用 100kg 载荷和直径 1.58mm 淬硬的钢球，求得的硬度，用于硬度较低的材料（如退火钢、铸铁等）。 HRC ：是采用 150kg 载荷和钻石锥压入器求得的硬度，用于硬度很高的材料（如淬火钢等）。 3 维氏硬度（ HV ） 以 120kg 以内的载荷和顶角为136 °的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷 值，即为维氏硬度值 (HV) 。 根据德国标准 DIN50150, 以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。 ?
硬度试验是机械性能试验中最简单易行的一种试验方法。为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。 实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。 下面是本站根据由实验得到的经验公式制作的快速计算器，有一定的实用价值，但在要求数据比较精确时，仍需要通过试验测得
国内外常用材料对照表
中国、美国、日本、德国常用相当材料对照表（仅供参考） 材料中国 (GB 、 JB)美国（ ASTM 、 ASME ）日本（ JIS）德国（ DIN ） 类别牌号标准号牌号标准号牌号标准号牌号数字表示法标准号碳GB912SA36ASTM SS400JIS G3101St37-2 1.0037DIN17100素Q235-B,C GB3274SA283GrC ASTM Rst37-2 1.0038DIN17100纲RsT37-3 1.0116DIN17100 SA285GrC ASTM SGV410JIS G3101HⅡ 1.0425DIN17155 20R GB6654SA516Gr60ASTM SB410JIS G3106Rst42 1.0498DIN17100 SA515Gr60ASTM SPV235JIS G3115 SA516Gr70ASTM SPV355JIS G311519Mn6 1.0473DIN17155 16MnR GB6654 SA662GrC ASTM 16MnDR GB3531SA516Gr70ASTM SLA325A JIS G3126TTST35N (-40 ℃ ) 09MnNiDR SA662GRC ASTM SLA325B JIS G3126TTST41V 1.0437SEW680 (-70 ℃ )GB3531 SA738ASTM 压力 容器SA737GrC ASTM 15MnVR GB6654 用钢SA612ASTM 12-1SA387SCMV2-1JIS G410913CrMo44 1.7335DIN17155 15GrMoR GB6654 12-2SA387SCMV2-2JIS G4109 11-1SA387SCMV3-1JIS G4109 14GrMoR GB6654 11-2SA387SCMV3-2JIS G4109 22-1SA387SCMV4-1JIS G410910CrMo910 1.7380DIN17155 12Gr2Mo1 22-2SA387SCMV4-2JIS G4109 5-1SA387SCMV6-1JIS G4109 1Gr5Mo 5-2SA387SCMV6-2JIS G4109 0Cr13GB4237410S SA240 SUS410S JIS G4304X6Cr13 1.4000DIN17440 SUS410S JIS G4305 X15Cr13 1.4024DIN17440 1Cr13GB4237410SA240SUS410JIS G4305 X10Cr13 1.1006DIN17440 0Cr13Al GB4237405SA240SUS405JIS G4305 304SA240SUS304JIS G4305X5CrNi1810 1.4301DIN17440 0Cr18Ni9GB4237 304H SA240 0Cr18Ni10Ti GB4237321SA240SUS321JIS G4305X6CrNiTi1810 1.4541DIN17440不锈 1Cr18Ni9Ti321H 钢板 00Cr19Ni10GB4237304L SA240SUS304L JIS G4305X2CrNi1911 1.4305DIN17440 316SA240SUS316JIS G4305X5CrNiMo17122 1.4401DIN17440 0Cr17Ni12Mo2GB4237 316H SA240X5CrNiMo17122 1.4401DIN17440 316L SA240SUS316L JIS G4305X2CrNiMo17132 1.4404DIN17440 00Cr17Ni14Mo2GB4237 X2CrNiMo18143 1.4435DIN17440 0Cr18Ni12Mo2Ti GB4237316Ti SA240X6CrNiMoTi17122 1.4571DIN17440 0Cr19Ni13Mo3GB4237317SA240SUS317JIS G4305 00Cr19Ni13Mo3GB4237317L SA240SUS317L JIS G4305
国内外材料对照表
钢板金属材料牌号对照 中国GB 日本JIS 美国ASTM 德国 钢种 牌号 牌号 标准号钢号 钢号 材料号 标准号 Q235-F SS41 G3101A36 USt37-2 1.0112 DIN17100Q235 SS41 G3101A283-C RSt37-2 1.0114 DIN17100Q255A SS50 G3101A283-D (RSt42-2) 1.0134 DIN17100 (A3R) SPV24 G3115A285-C 20g SB42 G3103A515.Cr60 HⅡ 1.0425 DIN17155(15g) SB35 G3103A515.Cr55 HⅠ 1.0345 DIN17155(25g) SB46 G3103A515.Cr65 HⅢ 1.0435 DIN17155 碳素 钢板 25 SM41A G3103 DIN17100 16Mn SM50-B.C G3106 St52-3 1.0841 DIN1715516MnR SM41B G3106A299/A537-Ⅰ.Ⅱ 17Mn4 19Mn5 1.0841 1.8045 16MngC SPV36 G3115 St52-3 15MnVR SPV36 (WELTEN50) G3115 A225Gr.A.B WStE39 1.8930 15MnVgC (A633-GR.B) 15MnVNTR (K-TEN62M) A302-GR.B 低合金 钢板 18MnMoNbR A533-Gr.A.I 16Mo SB46M G3103A204-Gr A.B 15 Mo3 1.5414 DIN17155 12CrMo SCMV1 G4109A387-Gr.2 15CrMo SCMV2 G4109A387-Gr.12 13 CrMo44 1.7335 DIN17155耐热 钢板 12Cr2Mo1 SVMV4 G4109 A387-Gr.22 10 Mo910 1.7362 DIN17155 16MnR SLA24B G3126 A516-Gr55 TTSTE26 1.0463 SEW089 15MnVR SLA33A A516-Gr60 TTSTE29 1.0488 低温 钢板 15MnVNTR A516-Gr65 A516-Gr70 TTSTE32 TTSTE36 1.0851 1.0859
国内外不锈钢牌号对照表常用
国内外不锈钢牌号对照表（常用）一.常用（无力学性能）
二:
奥氏体不锈钢 奥氏体不锈钢：在常温下具有奥氏体组织的不锈钢。钢中含Cr约18%、Ni 8% ~10%、C约0.1%时，具有稳定的奥氏体组织。奥氏体铬镍不锈钢包括著名的18Cr-8Ni钢和在此基础上增加Cr、Ni含量并加入Mo、Cu、Si、Nb、Ti等元素发展起来的高Cr-Ni系列钢。奥氏体不锈钢无磁性而且具有高韧性和塑性，但强度较低，不可能通过相变使之强化，仅能通过冷加工进行强化。如加入S，Ca，Se，Te等元素，则具有良好的易切削性。此类钢除耐氧化性酸介质腐蚀外，如果含有Mo、Cu等元素还能耐硫酸、磷酸以及甲酸、醋酸、尿素等的腐蚀。此类钢中的含碳量若低于0.03%或含Ti、Ni，就可显著提高其耐晶间腐蚀性能。高硅的奥氏体不锈钢浓硝酸肯有良好的耐蚀性。由于奥氏体不锈钢具有全面的和良好的综合性能，在各行各业中获得了广泛的应用。 奥氏体型钢 (1)1Cr17Mn6Ni15N；(2)1Cr18Mn8Ni5N；(3)1Cr18Ni9；(4)1Cr18Ni9Si3；(5)0 Cr18Ni9；(6)00Cr19Ni10；(7)0Cr19Ni9N；(8)0Cr19Ni10NbN；(9)00Cr18Ni10N；(1 0)1Cr18Ni12；(11) 0Cr23Ni13；(12)0Cr25Ni20；(13) 0Cr17Ni12Mo2；(14) 00Cr 17Ni14Mo2；(15) 0Cr17Ni12Mo2N；(16) 00Cr17Ni13Mo2N；(17) 1Cr18Ni12Mo 2Ti；(18) 0Cr18Ni12Mo2Ti；(19) 1Cr18Ni12Mo3Ti；(20) 0Cr18Ni12Mo3Ti；(21) 0Cr18Ni12Mo2Cu2；(22) 00Cr18Ni14Mo2Cu2；(23) 0Cr19Ni13Mo3；(24) 00Cr1 9Ni13Mo3；(25) 0Cr18Ni16Mo5；(26) 1Cr18Ni9Ti；(27) 0Cr18Ni10Ti；(28) 0Cr 18Ni11Nb；(29) 0Cr18Ni13Si4 1.概述 奥氏体不锈钢1913年在德国问世，在不锈钢中一直扮演着最重要的角色，其生产量和使用量约占不锈钢总产量及用量的70%。钢号也最多，当今我国常用奥氏体不锈钢的牌号就有40多个，最常见的就是18-8型。 定义：常温下具有奥氏体组织的不锈钢。 分类：Fe-Cr-Ni (主体) Fe-Cr-Mn 国内外牌号对比： GB(中国)ASTM(美国) JIS(日本) DIN(德国) 1Cr17Ni7 301 SUS301 X12CrNi177 1Cr18Ni9 302 SUS302 X12CrNi188 1Cr18Ni10 303 SUS303 X12CrNiS188 0Cr18Ni9 304 SUS304 X5CrNi189 0Cr19i10 304L SUS304L X2CrNi189 0Cr17Ni12Mo2 316 SUS316 X5CrNiMo1810 00Cr17Ni14Mo2 316L SUS316L X2CrNiMo1810 0Cr18Ni10Ti 321 SUS321 X10CrNiTi189 0Cr19Ni13Mo3 317 SUS317 X2CrNiMo1816
常用金属材料钢号对照表
附录A常用金属材料钢号对照表 钢材种类中国GB 美国ASME 日本JIS 德国DIN/欧洲EN 俄罗斯ГОСТ捷克CSN 碳钢 Q235A 20G SA-106A/B/C SA-210A/ C SA-283A/B/C/D STB42 St45.8/III HⅡ 20 20К 12022 低合金钢 15MoG SA-209 T1，T1a， T1b(20MoG) SA-335P1(20MoG) STBA12 15Mo3 16М150020 15CrMoG SA-213T12，T11 SA-335P12，P11 SA-182F12，F11 SA-387Gr.11，Gr.12 STBA22，STPA22 STBA23，STPA23 13CrMo44 15ХМ15121 12Cr2MoG SA-213T22 SA-335P22 SA-182F22 SA-387Gr.22,22L STBA24 STPA24 10CrMo910 - 15313 12CrMoVG - - 14MoV63 12ХМФ 15123 15128 12Cr1MoVG - - 12Cr1MoV 12ХМФ- 12Cr2MoWVTiB（G102）- - - - - 07Cr2MoW2VNbB SA-213T23 SA-335P23 HCM2S 住友7Cr W VMoNb9-6 - -
- SA-213T24 SA-335P24 - 7CrMoVTiB10-10 - - 15Ni1MnMoNbCu SA-213T36 SA-335P36 15NiCuMoNb5 (WB36) 15NiCuMoNb-5-6-4 - - 马氏体钢 10Cr9Mo1VNbN SA-213T91 SA-335P91 SA-182F91 SA-387Gr.91 STPA28 NF616 X10CrMoVNb9-1 - - 10Cr9Mo1W1VNbBN SA-213T911 SA-335P911 - X11CrMoWVNb9-1-1 E911 - - 10Cr9MoW2VNbBN SA-213T92 SA-335P92 SA-182F92 SA-387Gr.92 - X10CrWMoVNb9-2 - - 10Cr11MoW2VNbCu1BN SA-213T122 SA-335P122 SA-182F122 SA-387Gr.122 HCM12A 住友 SUS410J3DTB 三菱 - - - - - - X20CrMoV12-1 X20CrMoWV12-1 1Х12B2МФ 2Х12B2МФ - 奥氏体不锈钢 07Cr19Ni10 SA-213TP304H SUS304TB SUS304TP X5CrNi18-10 - - 10Cr18Ni9NbCu3BN SA-213S30432 Super304H 住友- - - 07Cr25Ni21NbN SA-213TP310HCbN S31042 - - - （HR3C）SA-213S31042 06Cr17Ni12Mo2 SA-213TP316/ TP316L SUS316 - - - 07Cr19Ni11Ti SA-213TP321 / TP321H SUS 321HTB X7CrNiTi18-10 - - 07Cr18Ni11Nb SA-213TP347/ TP347H SUS 347HTB X7CrNiNb18-10 - - 07Cr18Ni11NbFG SA-213TP347HFG - - - -