Shell Plating Contact Plating RoHS Compliant 4615-0-31-80-47-27-04-0200 - 300 μ" Tin (matte finish) over Nickel 30 μ" Gold over Nickel
CONTACT:
Contact Used: #47, Standard 6 Finger Contact
Current Rating = 4.5 Amps
BERYLLIUM COPPER ALLOY 172 (UNS C17200) per
ASTM B 194
Properties of BERYLLIUM COPPER:
Chemical composition: Cu 98.1%, Be 1.9%
Temper as stamped: TD01
Properties after heat treatment (TH01):
Hardness: 36-43 Rockwell C
Mechanical Life: 100 Cycles Min.
Density: .298 lbs/in3
Electrical Conductivity: 22% IACS*
Resistance: 10 miliohms Max
Operating Temperature: -55°C/+125°C
Melting point: 980°C/865°C (liquidus/solidus)
Stress Relaxation?: 96% of stress remains after 1,000 hours @ 100 oC ; 70% of stress remains after 1,000 hours @ 200 oC
*International Annealed Copper Standard, i.e. as a % of pure copper.
?Since BeCu loses its spring properties over time at high temperatures; it is rated for continuous use up to 150°C. For applications up to 300°C, Mill-Max offers many contacts in Beryllium Nickel. Contact Tech Support for more info.
SHELL MATERIAL:
BRASS ALLOY (UNS C36000) per ASTM B 16
Properties of BRASS ALLOY:
Chemical composition: Cu 61.5%, Zn 35.4%, Pb 3.1%?
Hardness as machined: 80-90 Rockwell B
Density: .307 lbs/in3
Electrical conductivity: 26% IACS*
Melting point: 900°C/885°C (liquidus/solidus)
?(3 to 4% lead is used to permit “free machining” and is permitted by EC Directive 2002/95Annex 6; so all pin materials are RoHS compliant)
*International Annealed Copper Standard, i.e. as a % of pure copper.