Synthesis of Unique Ultrathin Lamellar Mesostructured CoSe2-Amine (Protonated)Nanobelts in a Binary Solution

Min-Rui Gao,Wei-Tang Yao,Hong-Bin Yao,and Shu-Hong Yu*

Di V ision of Nanomaterials and Chemistry,Hefei National Laboratory for Physical Sciences at Microscale, Department of Chemistry,Uni V ersity of Science and Technology of China,Hefei,

Anhui230026,The People’s Republic of China

Received January22,2009;E-mail:shyu@https://www.wendangku.net/doc/157208420.html,

Inorganic-organic hybrid composites aroused a lot of recent interest from the viewpoints of both new properties and techno-logical applications.1Incorporation of two counterparts into a single structure may enhance or combine the superior electronic,magnetic, and optical feathers,rigidity,and thermal stability of inorganic frameworks with the structural diversity,?exibility,processability, and geometrical controllability of organic molecules.Recent advances show that novel hybrid II-VI semiconductors can be synthesized by incorporating segments(e.g.,a slab or chain)of a II-VI semiconductor,MQ,and organic spacers(L)in one structure via coordinate or convalent bonds.2These structures have a composition of[MQ(L)x](M)Mn,Zn,Cd;Q)S,Se,Te;L) mono-or diamine or hydrazine;x)0.5or1.0),wherein nanometer-sized components of identical size are arranged in a perfectly periodic crystal structure.2,3In addition,many literature reports describe the preparation of1D inorganic-organic hybrid nano-crystals,4e.g.,ZnSe(diethylenetriamine)0.5nanobelts,4a ZnS/N2H4,4b ZnS/cyclohexylamine,4c ZnS/amine,4d WO2.72(N6C123H136O22)0.04,4e GeO x/ethylenediamine nanowires,4f and Fe18S25(triethylenetetr-amine)14nanoribbons,4g because of their potential applications as building blocks for electronic and optical nanodevices.Since the ?rst discovery of mesoporous silica in1992,5numerous systems of mesoporous metal oxides6and porous semiconductors7have been reported so far.Only a few studies,however,have been focused toward synthesizing a semiconductor and its organic mesostructured composites,such as Ge,8GeS2,SnS2,CdS,and CdSe.9Additionally, how to synthesize a mesostrucured composite with a well-de?ned shape has been rarely reported.

As an important pyrite-type compound,CoSe2is known as a metallic conductor and exchange-enhanced Pauli paramagnent in its ground state with a Curie temperature,T c,of124K.10However, the extraordinary capability of CoSe2has rarely been researched in nanoscale materials primarily due to the limited availability of high-quality materials.Herein,we report a simple method for direct synthesis of the?rst mesostructed CoSe2-amine(protonated) nanobelts(amine)diethylenetriamine(DETA),triethylenetetra-mine(TETA),and tetraethylenepentamine(TEPA))in a binary solution under solvothermal conditions.

The CoSe2-amine(protonated)composite nanobelts were syn-thesized by solvothermal reaction of Co(Ac)2·H2O and Na2SeO3 in a mixed solution(40mL)with a volume ratio of V DETA/V DIW) 2:1(DIW)deionzed water)at180°C for16h(see Supporting Information,SI).The powder X-ray diffraction(XRD)of the samples was recorded in a2θrange of3°-70°.The peaks of00l′can be indexed as(001)and(002)with lattice spacings of1.10 and0.55nm,respectively(Figure1a).The other wide-angle re?ections can be readily indexed to a pure primitive cubic phase of CoSe2structure with a lattice parameter of a)0.586nm(JCPDS 9-234).The broadening width of all re?ections and the disappear-ance of some re?ections should be related to the very thin layered structure of the obtained product.11Energy dispersive X-ray spectrum(EDS)analysis shows the mean atom ratio of Co/Se is 1:2(SI,Figure S1).A room temperature Raman spectrum of the sample also con?rms the formation of a cubic CoSe2phase12(SI, Figure S2).

Scanning electron microscopy(SEM)images in Figure2a indicate that the sample is composed of nanobelts with widths of 100-500nm and lengths up to several tens of micrometers.The transmission electron microscopy(TEM)image in Figure2b shows that the nanobelts are?exible,smooth,thin,and almost transparent. The selected-area electron diffraction(SAED)pattern taken on a typical nanobelt shows the single-crystalline nature.The corre-sponding high-resolution TEM image in Figure2d shows resolved lattice fringes of(210)planes with a spacing of2.68?,which depicts that the growth direction is[210].

Similarly,substitution of DETA by TETA and TEPA in CoSe2-DETA(protonated)can also generate CoSe2-TETA and CoSe2-TEPA nanobelts with single crystal structures(Figure1b,c,and SI,Figure S3).It should be noted that the CoSe2-TETA(or TEPA) mesostructured nanobelts have almost the same interlamellar distances with that for CoSe2-DETA nanobelts. Interestingly,a lateral view of the as-obtained nanobelts along the thickness direction clearly shows well-de?ned

multilayered Figure1.XRD patterns of the samples prepared at180°C for16h in different binary solution.(a)CoSe2-DETA nanobelts,V TETA/V DIW)2:1.

(b)CoSe2-TEPA nanobelts,V TEPA/V DIW)2:1.(c)CoSe2-TETA nanobelts, V TETA/V DIW)

2:1.

Figure2.(a,b)SEM and TEM images of the morphology of lamellar mesostructured CoSe2-DETA nanobelts,respectively.(c)HRTEM image of a single lamellar mesostructured CoSe2-DETA nanobelt.Inset shows the corresponding SAED pattern.(d)A typical HRTEM image taken on the marked part in

(c).

Published on Web05/15/2009

10.1021/ja900506x CCC:$40.75 2009American Chemical Society 74869J.AM.CHEM.SOC.2009,131,7486–7487

nanostructures,and the direction of the strips is parallel to the [210]direction (Figure 3).The interlayer distance can be estimated to be ～1.08nm,which is in good agreement with that detected by XRD.It is worth noting that the observed thickness of a single CoSe 2layer is ～0.57nm which is equal to its lattice parameter (Figure 3c).To the best of our knowledge,this kind of multilayered mesostructured nanobelt is totally different from other mesostruc-tured 1D nanomaterials obsersed previously.4d,f

An FT-IR spectrum shows that the vibration bands of -CH 2-,-NH 2,C -N,and -NH suggest the existence of DETA in the product (SI,Figure S4).Compared with that of pure DETA,the weak intensity of all vibrations and the absence of several bands presumably are due to the rather low content of DETA in the hybrid structure.The binding energy of N1s is identi?ed at 400.5eV,which is close to the binding energy of protonated amine (401.1eV)13and also suggests the presence of DETA in the product (SI,Figure S5).X-ray ?uorescence (XRF)analysis further con?rms the existence of the low content of DETA in the product (SI,Figure S6).Thermal gravimetric analysis (TGA)shows that ～4.2wt %DETA remained in the sample (SI,Figure S7).Removal of the amine at elevated temperature will result in the formation of pure phase CoSe 2nanobelts (SI,Figure S8).

The in?uence of reaction time and temperature on the formation of such mesostructures and morphology has been carefully inves-tigated.Well-de?ned CoSe 2-DETA (protonated)mesostructured nanobelts can only be obtained in a mixed solvent within a very narrow volume ratio range of V DETA /V DIW (SI,Table S1,Figures S9,S10).Increasing the volume ratio of V DETA /V DIW up to 2:5or 1:6will result in the formation of a pure CoSe 2phase only.The favorable conditions for the formation of such nanobelts are to initiate the reaction at 180°C for 16h in a mixed solvent with a volume ratio of V DETA /V DIW )2:1.

The formation mechanism of the above unique mesostructured nanobelts has been proposed in Scheme 1.First,some amine molecules used here are protonated by reaction with water under solvothermal conditions at 180°C and form positively charged ammonium ions.Then,the protonated amine molecules are incorporated into neighboring CoSe 2layers by coordination with Se.Here,the amine with a linear con?guration acts as a template

molecule,which not only leads to the new mesostructured nanobelts but also induces anisotropic growth of 1D nanostructures.This is analogous to the so-called solvent coordination molecular template mechanism.14Furthermore,the interlamellar distances still keep constant although other amines with different chain lengths were used,because the protonated amine molecules are incorporated into the inorganic framework by taking a horizontal con?guration from the viewpoint of energy minimization (SI,Figure S11).The experiments showed that the CoSe 2-DETA nanobelts are stable in pure acetic acid but not stable in week alkali solution,which can further con?rm that the occurrence of protonation of amine molecules played a key role in the formation of such mesostructures (SI,Figures S12,S13).

In summary,unique ultrathin CoSe 2-amine (protonated)meso-structured nanobelts with multiple stacked layers which are highly parallel to the axial direction have been ?rst prepared in a binary solution of organic amine and water under mild solvothermal conditions.This synthesis strategy may open new avenues toward the syntheses of other mesostructured nanomaterials with unique shapes and structural features,which may bring new nontrivial functionalities.

Acknowledgment.This work was supported by the NSFC (50732006,20621061,20671085,20701035),2005CB623601,and the Partner Group of the CAS-MPG.

Supporting Information Available:Preparation procedures and characterization,and TEM,XRD,HRTEM,FT-IR.This material is available free of charge via the Internet at https://www.wendangku.net/doc/157208420.html,.References

(1)(a)Sanchez,C.;Lebeau,B.;Chaput,F.;Boilot,J.P.Ad V .Mater.2003,

15,1969.(b)Sanchez,C.;Julia ′n,B.;Belleville,P.;Popall,M.J.Mater.Chem.2005,15,3559.(c)Yao,W.T.;Yu,S.H.Ad V .Funct.Mater.2008,18,3357.

(2)(a)Huang,X.Y.;Li,J.;Fu,H.X.J.Am.Chem.Soc.2000,122,8789.(b)

Heulings,H.R.;Huang,X.Y.;Li,J.;Yuen,T.;Lin,C.L.Nano Lett.2001,1,521.(c)Huang,X.Y.;Li,J.J.Am.Chem.Soc.2007,129,3157.(d)Yu,S.H.;Yoshimura,M.Ad V .Mater.2002,14,296.

(3)(a)Huang,X.Y.;Li,J.;Zhang,Y.;Mascarenhas,A.J.Am.Chem.Soc.

2003,125,7049.(b)Huang,X.Y.;Heulings,H.R.;Le,V.;Li,J.Chem.Mater.2001,13,3754.

(4)(a)Yao,W.T.;Yu,S.H.;Huang,X.Y.;Jiang,J.;Zhao,L.Q.;Pan,L.;

Li,J.Ad V .Mater.2005,17,2799.(b)Dong,Y.J.;Peng,Q.;Li,https://www.wendangku.net/doc/157208420.html,m.2004,7,370.(c)Fan,L.B.;Song,H.W.;Zhao,H.F.;Pan,G.H.;Yu,H.Q.;Bai,X.;Li,S.W.;Lei,Y.Q.;Dai,Q.L.;Qin,R.F.;Wang,T.;Dong,B.;Zheng,Z.H.;Ren,X.G.J.Phys.Chem.B 2006,110,12948.(d)Yao,W.T.;Yu,S.H.;Wu,Q.S.Ad V .Funct.Mater.2007,17,623.(e)Polleux,J.;Pinna,N.;Antonietti,M.;Nieder-berger,M.J.Am.Chem.Soc.2005,127,15595.(f)Gao,Q.S.;Chen,P.;Zhang,Y.H.;Tang,Y.Ad V .Mater.2008,20,1837.(g)Zang,Z.A.;Yao,H.B.;Zhou,Y.X.;Yao,W.T.;Yu,S.H.Chem.Mater.2008,20,4749.(5)Kresge,C.T.;Leonowicz,M.E.;Roth,W.J.;Vartuli,J.C.;Beck,J.S.

Nature 1992,359,710.

(6)Yang,P.D.;Zhao,D.Y.;Margolese,D.I.;Chmelka,B.F.;Stucky,G.D.

Nature 1998,396,152.

(7)(a)Mohanan,J.L.;Arachchige,I.U.;Brock,S.L.Science 2005,307,

397.(b)Bag,S.;Trikalitis,P.N.;Chupas,P.J.;Armatas,G.S.;Kanatzidis,M.G.Science 2007,317,490.

(8)Armatas,G.S.;Kanatzidis,M.G.Science 2006,313,817.

(9)(a)Maclachlan,M.J.;Coombs,N.;Ozin,G.A.Nature 1999,397,681.

(b)Scott,R.W.J.;Maclachlan,M.J.;Ozin,G.A.Curr.Opin.Solid State Mater.Sci.1999,4,113.(c)Braun,P.V.;Osenar,P.;Stupp,S.I.Nature 1996,380,325.(d)Neeraj.;Rao,C.N.R.J.Mater.Chem.1998,8,279.(10)(a)Sato,H.;Nagasaki,F.;Kani,Y.;Senba,S.;Ueda,Y.;Kimura,A.;

Taniguchi,M.Solid State Commun.2001,118,563.(b)Waki,S.;Kasai,N.;Ogawa,S.Solid State Commun.1982,41,835.(c)Inoue,N.;Yasuoka,H.Solid State Commun.1979,30,341.

(11)Polleux,J.;Antonietti,M.;Niederberger,M.J.Mater.Chem.2006,16,

3969.

(12)Campos,C.E.M.;de Lima,J.C.;Grandi,T.A.;Machado,K.D.;Pizani,

P.S.Physica B 2002,324,409.

(13)Nakayama,M.;Hoyashita,R.;Komatsu,H.;Muneyama,E.;Shoda,K.;

Kunishige,https://www.wendangku.net/doc/157208420.html,ngmuir 2007,23,3462.

(14)Li,Y.D.;Liao,H.W.;Ding,Y.;Fan,Y.;Zhang,Y.;Qian,Y.T.Inorg.

Chem.1999,38,1382.

JA900506X

Figure 3.(a -c)Typical HRTEM images viewed along the lateral thickness direction,which were taken on individual nanobelts.

Scheme 1.Formation of CoSe 2-DETA Mesostructured Nanobelts

a

a

The proposed formation mechanism of the CoSe 2-DETA mesostructured nanobelts.Red,white,blue,gray,pink,and yellow balls correspond to O,H,N,C,Co,and Se atoms,respectively.Hydrogen atoms are omitted for clarity in the structure.

J.AM.CHEM.SOC.

9

VOL.131,NO.22,20097487

C O M M U N I C A T I O N S