晶体硅太阳能电池无网结网版用正银浆料研究

第37卷第5期电子元件与材料V ol.37 No.5 2018年5月ELECTRONIC COMPONENTS AND MATERIALS May 2018

晶体硅太阳能电池无网结网版用正银浆料研究

刘晓巍1，陈栋2，付明3，范琳2

（1. 宁波尤利卡太阳能科技发展有限公司，浙江 宁波 315100；2. 武汉优乐光电科技有限公司，湖北 武汉 430206；3. 华中科技大学 光学与电子信息学院，湖北 武汉 430074）

摘要: 采用水浴加热法制备有机载体，利用该载体制备硅太阳能电池正面银浆。研究了浆料的有机载体对电池片正面细栅线高宽比的影响，以及最终对电池片转换效率的影响；同时也探讨了不同玻璃体系在不同方阻的电池片上的差异性。通过SEM和TGA/DSC分析手段，分析栅线表面形貌、正银浆料无机体系以及硅片方阻等对电池片效率产生影响的机理。结果表明栅线表面平整且宽度小的电池片效率最高；含铅玻璃体系适应高中低方阻的电池片，而无铅玻璃体系只适应中低方阻的电池片。最终设计出适合无网结网版印刷特性的正银浆料，同时匹配相应方阻，提高了电池片效率。

关键词: 晶体硅太阳能电池；无网结网版；有机载体；玻璃体系；方阻；转换效率

doi: 10.14106/https://www.wendangku.net/doc/2a9608002.html,ki.1001-2028.2018.05.008

中图分类号: TN41 文献标识码:A 文章编号:1001-2028（2018）05-0047-05

Front silver paste of crystalline silicon solar cells for

no-mesh network version

LIU Xiaowei1, CHEN Dong2, FU Ming3, FAN Lin2

(1. Ningbo Ulica Solar Science & Technology Co., Ltd, Ningbo 315100, Zhejiang Province, China; 2. Wuhan

Supernano Optoelectronic Co., Ltd, Wuhan 430206, China; 3. School of Optics and Electronics Information, Huazhong

University of Science and Technology, Wuhan 430074, China)

Abstract: Organic carrier was developed by heating in water-bath, and the front silver paste of crystalline silicon solar cell was prepared by using above organic carrier. The effect of organic carrier on the ratio of height to width of the grid lines was studied. The relationship between the efficiency of the solar cells and glass systems was analyzed. With the help of scanning electron microscope (SEM) and thermogravimetric analysis and differential scanning calorimetry (TGA/DSC), it is found that, the efficiency of the solar cells is closely related with the surface topography of the grid lines, glass frits of paste and square resistance of silicon cells. In order to improve the efficiency of solar cells, it is necessary to select a front silver paste which printed well on the no-mesh network version, and it is necessary to adjust the square resistance of solar cells to match the front silver paste.

Key words: crystalline silicon solar cell; no-mesh network version; organic carrier; glass system; square resistance;

conversion efficiency

晶体硅太阳能电池是利用光生伏特效应的半导体器件，其制作工艺一般在P型硅衬底上扩散N型硅形成太阳电池雏形，在硅片表面镀减反射膜以减少对太阳光的反射，通过丝网印刷厚膜电子浆料，以及链式炉烧结工艺制作上下电极[1]，如图1所示。正面银浆主要由金属银粉、有机载体、无机玻璃粉和添加剂等组成，有机载体直接影响浆料的丝网印刷性能，对电池的效率有直接影响；玻璃粉在正银