题目The preparation of TiO2 aerogel by

ambient pressure drying and its performance of

photocatalytic degradation of oily wastewater

学生姓名学号

教学院系研究生学院

专业年级2013级材料化学工程

指导教师职称副教授

单位

辅导教师职称

单位材料科学与工程学院

完成日期2013 年12 月 1 日

摘要

以钛酸四丁酯(TBT)为原料, 利用溶胶–凝胶法、小孔干燥和老化液浸泡工艺在常压下制备出了完整、无开裂的TiO2 气凝胶块体. 研究了小孔干燥和老化液浸泡技术对常压制备TiO2 气凝胶的影响, 研究结果表明: 小孔干燥能够降低TiO2 醇凝胶干燥过程中所受的不均匀收缩应力, 而TBT 醇溶液和TEOS 醇溶液浸泡处理, 能够增强凝胶的骨架强度, 有助于减轻凝胶在干燥过程中的收缩和开裂, 制备出完整的高性能TiO2 气凝胶块体. 基于小孔干燥和TEOS 乙醇溶液浸泡老化处理, 制备得到的高性能完整TiO2 气凝胶块体, 其密度为0.184 g/cm3, 比表面积达389.5 m2/g. 用高温煅烧后的锐钛矿相TiO2 气凝胶催化降解渤海原油污水模拟溶液, 在TiO2 气凝胶加入量为 400 mg/L 的情况下, 90 min 内对渤海原油污水的去除率最高可达91%.

关键词：TiO2 气凝胶; 常压; 小孔干燥; 老化液; 光催化; 原油降解

Abstract

The monolithic TiO2 aerogel was sucessfully synthesized at ambient pressure through

technique with TBT as the raw material and its photocatalyst property for

was investigated .

During the ambient drying process, aging liquor and pinhole drying technology were found to be critical to the properties of TiO2 aerogels.

in the drying process and the TEOS-Ethanol or TBT-Ethanol solution as the liquor for TiO2 wet-gel could enhance the strength of TiO2 gel skeleton .these effects, and the high-performance TiO2 aerogel monolith was eventually achieved. The most integrated TiO2 aerogel block exhibited low density (0.184 g/cm3) and high specific surface area (389.5 m2/g). By calcinations at high temperature, the TiO2

changed from amorphous to anatase structure. The photocatalytic properties of heat-treated TiO2 aerogels were investigated via aqueous emulsion of crude oil in the Bohai Sea. The results of experiments showed that the catalytic degradation rate was up to 91% with

addition of TiO2 aerogel of 400 mg/L.

Key words: crude oil degradation

Contents

摘要 (2)

Abstract (3)

1. Introduction (5)

2. Literature review (6)

3.Methodology (6)

4. Result and Discussion (8)

5. Conclusion (15)

Reference (16)

1.Introduction

the development of modern industry, society and economy,’the demand for energy is growing, the oil exploration, transportation and refining process generated a lot of oily wastewater, causing serious a serious impact on the environment .To make a effective treatment of oily wastewater has become an urgent need to solve the environmental problems.The traditional youngest segment ( ramp degreasing, plus flotation select and walnut shell filter oil ) and other physical treatment , although ,can remove a lot of oil in oily water , but the treated sewage is still a high oil content. What is more, the traditional processing techniques , stay a long time , large equipment volume , large dependence on the demulsifier ,is not suitable for the development of marginal oil fields as needed. Since 1972,

Fujishima and Honda et al [1] found that TiO 2 surface water by radiation can continued oxidation-reduction reaction, The photocatalytic reaction based bandgap semiconductor materials has been more widely appreciated by people. Because of the high photocatalytic efficiency , non-toxic , non-polluting ,low price and other features,in recent years, the useing of nano-TiO2 to make a photocatalytic degradation of various organic and inorganic pollutants for environmental pollution, aroused great interest of researchers [4-5] . Since 2002 Ziolli et al [6 ] reported a nano TiO2 photocatalytic degradation of the performance of the Brazilian oil sewage , subsequently many scholars [7-8]studied experimentally,they found that nano-TiO2 has a very excellent photocatalytic degradation performance to the oily wastewater : speed degradation , high degradation rate , low energy consumption , mild reaction conditions , simple operation , wide application, no secondary pollution .But the nano- TiO2 is difficult to be recycled , difficult to promote practical application in industry.

For this reason, in recent years many people carried out a load TiO 2 and a

photocatalytic TiO 2 films research [ 8-9 ] , These methods can solve the problem of recovery of the TiO 2, but reduces the effective surface area of TiO2, thereby reducing the photocatalytic efficiency.

2.Literature review

Nano- TiO2 aerogel is a porous material ,not only has the independent features of nano TiO2 nanoparticles but also has ultra-high surface area ,and it can be prepared in a complete block structure, which can be solved the problem of difficult to recover when used as a catalyst [ 10 ] , but the traditional TiO2 aerogel were prepared by supercritical drying process , which is high production cost , poor security, and difficult industrial production .[ 11-12 ] .In recent years , solvent replacement ,surface

modification, technology made a breakthrough [ 13-14 ] , so that researchers

explore the ambient pressure drying for preparing SiO2 aerogel [ 15-16 ] .

the reason that the network skeleton of TiO2is weaker than the SiO2. In addition TiO2 aerogel Shrinked and cracked serious , it has been difficult to prepare complete at atmospheric pressure. This work treated TBT as titanium source , based on the sol -

with a dry hole and the old of liquid immersion technique

at atmospheric pressure drying complete no cracking of TiO2 put it to the

crude sewage, and achieved good results.

3.1 Preparation of TiO2 aerogels

5 mL of tetrabutyltitanate (TBT, AR, Beijing Chemical test Agent Factory) was dissolved in 15 mL of anhydrous ethanol (AR, West Long Chemical Reagent),Then added 0.5 mL of glacial acetic acid, magnetic stirring to form solution A. 2 mL of deionized water was added 10 mL of anhydrous ethanol, was stirred to form solution B . Then B solution was added dropwise to a state of stirring solution A. After A was formed sol, add 2 mL formamide (AR, of West Long Learn Reagent Factory) as a dry chemical control agents. After continue stirring for 3 min, injected into the sol in a cylindrical polypropylene molds, and the mold was sealed with plastic wrap. After the rest period of time at room temperature, then we can get the milky TiO2 alcohol gel.

Place gel TiO2 alcohol at room temperature for 1 day, put it into the anhydrous

were then immersed in absolute ethanol, tetrabutyl titanate Ester (TBT) solution of alcohol (ethanol and the volume ratio of 10:1 TBT),tetraethoxysilane (TEOS)in an alcohol solution (by volume of ethanol and TEOS 10:1), and in an environment of 50 ℃soaking 3 d, more daily for once soaked solution gel was

soaked after treatment with anhydrous alcohol washed three times, each time to soak at least 24 h at 50 ℃ environment, soak the gel in a solution to the remaining clean. After washing TiO2alcohol gel placed in an open container or hole polypropylene (container c over open a φ1 ~ 2 mm hole) and then turn on the TiO2 alcogel room temperature, 40 ℃, 50 ℃, 60 ℃, 70 ℃, 80 ℃ under various drying 2 d, Then we can get dried TiO2 airgel blocks.

3.2 Photocatalytic TiO2 airgel performance test

Sodium naphthenate as emulsifier, the Bohai oil (heavy oil) emulsion to 100 mg / L of oily wastewater simulation solution each time taking 0.16 g calcined after crystallization firing TiO2 airgel was added to a mixture of 400 mL water,and kept stirred using a stirrer while open excitation light source (a

100 W high-pressure mercury lamp and three 8 W UV lamp (254 nm)).Every so often take a certain volume of the mixture, still in the dark put 2 h later, supernatant was extracted with an equal volume of chloroform its in oil, and then centrifuged at 2500 r / min speed of from Heart 15 min, supernatant using UV-2802PC UV - can see spectrophotometer test solution concentration of crude oil, and then according to the formula as follow can be calculated at any time illumination of the Bohai oil TiO2 aerogels The degradation rate.

C t/C o

-1

%

100

/

Ct

-

Co

%=

?

=Co

）

（

η

In the formula, η% said oil degradation rate at time t, C0 is mixed with water the concentration of a mixed solution of the initial time, Ct is adding TiO2 aerogels, open concentration at time t after the mixture of oil and water sources.

4.Result and Discussion

4.1 Effect of atmospheric holes dried preparation of TiO2 aerogels

and container holes TiO 2 gel. From Fig.1,in general open container the drying TiO2 gel broken into many small pieces, shrunk serious; in the small port container,the drying TiO2 gel looked more complete,only in the middle of the had cracks, and the Shrinkage was l ess than the former.

Fig.1 Photographs of TiO2 aerogel dryed at ambient pressure (a) Open container; (b) Pinhole container

the two kinds of TiO2 gel which achieved in diffierent conditions. From the data of the table , compared with an open container the aerogels obtained in

holes drying method having a lower density and higher specific surface area (167.5 m2 / g). The results indicats that the holes drying method has a good effect to prevent the gel from Shrinkage and cracking. This is mainly due to the drying rate of the gel and the partial pressure of the ethanol vapor. In an open container , the partial pressure of the ethanol in the container was the same with the environment, which was much lower than ethanol saturated vapor pressure , so the evaporation rate of ethanol is quickly, and the skeleton structure of alcohol gel is exposed to the large instantaneous stress. If the skeleton structure was uneven, the gel would be subject to greater uneven stress and then crack; but in the hole container, for the ethanol molecules evaporated from alcogel cannot spread to the external environment soon, the ethanol steam partial pressure in the container gets closer and closer to the saturated vapor pressure along with the evaporation of fluid ethanol in the gel pores. Thus the evaporation speed of the ethanol and drying speed of alcogel were reduced, which decreased the gel contraction and lowered the possibility of cracking, because the instantaneous compressive stress of the gel network skeleton also has been reduced in the whole drying process of alcogel.

4.2 The function of the aging soaking to the atmospheric drying TiO2 aerogels

The Fig.2 are the TiO2 gels used ethanol, TBT / ethanol solution, TEOS / ethanol solution as aging conservation soaking respectively, and at hole pressure drying. In pure ethanol solution, the TiO2 is translucentthe; and after soaking dried in the TBT and TEOS alcohol, the TiO2 aerogel is pale yellow and completely opaque. What is more, the TiO2 aerogel soaking dried in TBT / ethanol solution cracked into two parts along the center of the sample, and the TiO2 which was soaking

dried in the

TEOS/ethanol had a perfect appearance and no cracks.

Fig.2 Photographs of TiO2 aerogel aged in different liquors (a) Ethanol; (b) TBT-Ethanol solution;

(c) TEOS-Ethanol

Table 2 lists the different aging immersion liquid was prepared TiO2 physical performance parameters of airgel, seen from the data in the table, after TBT after the ethanol solution and soaking TEOS ethanol solution, TiO2 alcohol condensate glue drying shrinkage than pure ethanol produced by soaking samples significantly reduced, airgel prepared by soaking only significantly lower than the density of pure ethanol after drying the airgel samples, the specific surface area is soaked in pure ethanol a substantial increase in the airgel sample, which shows that TBT ethanol solution and TEOS solution in ethanol solution as aging, can be significantly reduced wet TiO2 gel contraction in atmospheric drying process, effectively preventing alcohol gel cracking during the drying process, especially upon aging as TEOS conservation ethanol solution was prepared to give a complete, non-cracking of the

prepared TiO2 the body, the density of only 0.184 g/cm3, a specific surface area of 389.5 m2 / g. Such as density and Kucheyev the airgel blocks [17] using CO2 super- TiO2 critical density complete the drying process of the preparation of airgel blocks similar (0.18 g/cm3), the specific surface area above the supercritical drying process technology the specific surface area of aerogels prepared (290 m2 / g).

TEOS alcohol solution and TBT alcohol solution as a reason for aging solution TiO2 backbone can improve the strength of the gel , the gel is due to TiO2 porous network node consists of a tiny skeleton of TiO2 particles composed of isomers , between colloidal particles by Ti-O-Ti bonds, hydrogen bonds and van der wales bonded together , the pores in the gel with a small amount of residual water molecules on the surface of colloidal particles and pore walls , then there are a lot of the Ti-OH group when TiO2 gel was immersed in an alcohol solution of TBT TEOS or alcoholic solution , and the solution of TEOS molecules and TBT molecules will diffuse into the pores of the gel , the residual water molecules across hydrolysis reaction of formula (2) or ( 3 ) shown in hydrolysis reaction intermediate the product TiO (OH) 2 or SiO (OH) 2 addition to the self-condensation reaction product occurs a new SiO2 colloid or TiO2 particles filled in the pores of the gel or the network skeleton, skeleton structure of the gel network play support and enhance external effect, but also the surface of the colloidal particles may be Ti-OH group occurs ( 5) condensation reaction represented by the formula ( 4 ) and , between the gel particles generated in the new the Ti-O-Ti bond or Si-O-Ti bond , the TiO2 particles with gel Ti-O-Ti bond or Si-O-Ti bond together , because the Ti-O-Ti bond and Si-O-Ti bond has a strong binding force , but also on TiO2 gel network played a skeleton network enhancement .

(2)

(3)

(4)

(5)

Figure 3 is a different aging after soaking liquid preparation obtained TiO2 FT-IR spectra of the airgel . Ethanol to pure alcohol and TBT aging the liquid immersion liquid was prepared as a sample , the two -phase IR spectrum recently, a strong absorption at 480 to 533 cm-1peak is near the Ti-O bond stretching vibration absorption, is characteristic absorption peak of TiO2 absorption at 1035 cm-1 Closing peak is C-OH stretching vibration absorption , 1407 cm-1 absorption at Mainly closed by bending carboxyl (-COOH) of the C-O stretching and -OH 1581 cm-1 (1545 cm-1) to absorb vibration caused mainly at the from N-H bending vibration absorption and C-N bond stretching vibration absorption stack plus , these N-H bond , C-N bond , carboxyl groups mainly from adsorbed on the pore walls of the airgel formamide , acetic acid, other organic stars promoter, the absorption peak at 2362 cm-1 was adsorbed TiO2 airgel C-O deformation vibration of the walls of a small amount of mesoporous CO2 molecules , 3165 ( 3185 ) ~ 3400 cm-1 broad absorption peak at airgel table symmetric and antisymmetric adsorbed surface hydroxyl group or water molecules in the O-H bond stretch vibration absorbing

reduction [ 18 ]. Immersion aging alcohol solution was prepared as in TBT Samples in 2926 and 2957 cm-1 and two peaks , the major from the C-H bond in the residual organic molecules -CH2- groups of stretching vibration absorption and -CH3 stretching groups in the C-H bond absorption.

Fig. 3 FT-IR spectra of TiO2 aerogel aged in different liquors (a) Pure Ethanol; (b) TBT-Ethanol;

(c) TEOS-Ethanol

4.3 Thermal stability of the atmospheric drying TiO2 aerogels

The ethanol solution , TBT alcohol solution , TEOS solution immersion of the alcohol TiO2 aerogels discharge processing in a muffle furnace ,respectively, at 480℃, under calcined at 600 ℃ 4 h, after calcination , all three airgel samples remain block Figure 4 is an XRD pattern of the three samples before and after calcination For TBT pure ethanol alcohol solution and soaked samples after 480 ℃ calcined after burning, the sample is completely transformed into the anatase phase , after calcination at 600℃ , a clear diffraction peak of the rutile phase in the XRD pattern shows some

To change rutile TiO2 . TEOS alcohol solution soak for at reasonable sample after 480℃ calcination , will remain the same for the amorphous phase ,appear in the XRD pattern of anatase samples calcined at 600 ℃diffraction peaks , but not rutile production. Thus , TEOS dissolved prepared by soaking liquid phase transition temperature of TiO2 aerogels TBT than pure ethanol alcohol solution and soaking

place to soak aging preparation of sample processing phase transition temperature is high, which is due to the TEOS solution as the aging process of soaking TiO2 gel , forming a large number of Si-O-Ti bond, TiO2 phase change can be suppressed to improve the gas TiO2 Gel thermal stability [ 15 ] .

Fig. 4 XRD patterns of TiO2 aerogel calcined at different temperatures TiO2 aerogel aged in (a) ethanol; (b) TBT-ethanol; (c) TEOS-ethanol

4.4 The photocatalytic properties of different aging soaking liquid preparation of

TiO2 aeroges

Treat the calcined anatase phase TiO2 aerogels as a photocatalyst , test its photocatalytic degradation of performance of the Bohai Sea crude sewage. Figure 5 is Array the photocatalytic degradation curves for bohai oil products by TiO2 aerogels prepared

in different aging soaking ( The relative concentration of crude oil (C/C0)% -. illumination time curve ). As can be seen from figure , when the gel as a photocatalyst to decompose Bohai oil sewage, at the beginning of the bright lights, the concentration of crude oil in the mixture solution declined quickly, then gradually slows. Compared the three different degradation curves of the TiO2 aerogels, the degradation ability and the rate is increaing from alcohol solution to TEOS alcohol/solution. The main reason for this phenomenon is the difference of the surface area. As we know, the process of organic degradation contained the adsorption of the organic and the oxidation of the organic by the electron - hole pairs producted UV excitation. So the larger the surface area of the TiO2 aerogels the stronger adsorption capacity for organic molecules, as a result, the higher catalytic efficiency and the faster degradation rate. The table 3 lists the different surface area and catalytic

degradation rate at 90min which was prepared by different aging soaking liquid and

calcined in a high temperature. Among them, the sample which was prepared by the

TEOS solution and calcined into anatase still had a high surfacethe area up to 210.4m2/g, while the sample prepared by TBT and ethanol only had 49.8m2/g and 15.8m2/g respectively. The corresponding degradation rate of 90 min was 91 %, 87 %, 79 % respectively. This shows that the gegradation efficiency of the Bohai Oil has a certain relationship to the surface area.

Fig. 5 Photocatalytic degradation curve of oily wastewater

1 ) Firstly, a small hole drying method

stress, shrinkage and cracking of the TiO2 aerogel. The process helps to

2 ) In addition,t he using of TBT and TEOS solution as a aging solution can enhance the skeleton strength of the TiO2 glue , reduce the shrinkage and cracking of the TiO2 aerogel during the drying process. As a result,we can achieve a Complete block with high surface area, especially the TEOS.

3 ) Moreover, using TEOS alcohol solution as a aging solution, because of the

forming of the Si-O-Ti bond, it can prevent the phase transition and improve the

thermal stability of TiO2 aerogels.

4 ) Finally, the TiO2 aerogels after calcination into anatase phase by high temperature has a good photocatalytic degradation. The degradation rate and the degradation speed have a great reletionship to the surface area.

Acknowledgement

The authors are grateful to National Natural Science Foundation of China for nancial support .

Reference

[1] Fujishima A, Honda K. Electrochemical photolysis of water at a semiconductor

electrode. Nature, 1972, 238: 37–38.

[2] Chuangchote S, Jitputti J, Sagawa T, et al. Photocatalytic Activity for Hydrogen

Evolution of Electrospun TiO2 Nanofibers. Applied Materials andInterfaces,2009, 1(5): 1140–1143.

[3] Guo Peng, Liu Chun-Yan, Gao Min, et al. Effect of ZSM-5 crystal size on

properties of supported TiO2 photocatalyst. Chinese Journal of Catalysis, 2010, 31(5): 573–578.

[4] Kim M I, Park D W, Park S W, et al. Selective oxidation of hydrogen sulfide

containing excess water and ammonia over vanadia–titania aerogel catalysts.

Catalysis Today, 2006, 111(3/4): 212–216.

[5] Jing Wen-Heng, Wang Wei-Gang, Xing Wei-Hong. Preparation and photocatalytic

activity of macro-mesoporous N-doped TiO2. Chinese Journal of Catalysis, 2009, 30(5): 426–432.

[6] Ziolli R L, Jardim W F. Photocatalytic decompsition of seawater-soluble crude oil

fractions using high surface areacolloid nanoparticles of TiO2. Journal of Photochemistry and Photobiology a-Chemistry, 2002, 147(3): 205–212.

[7] Hsu Y Y, Hsiung T L, Wang H P, et al. Photocatalytic degradation of spill oils on

TiO2 nanotube thin films. Marine Pollution Bulletin, 2008, 57(6-12): 873–876.

[8] Liao Zhen-Hua, Chen Jian-Jun, Yao Ke-Fu, et al. Preparation and characterization

of nanometer-sized magnetic photocatalyst TiO2/SiO2/Fe3O4. Journal of Inorganic Materials, 2004, 19(4): 749–754.

[9] Addamo M, Augugliaro V, Paola A D, et al. Photocatalytic thin films of TiO2

formed by a Sol–Gel process using titanium tetraisopropoxide as the precursor.

Thin Solid Films, 2008, 516(12):3802–3807.

[10] Akpan U G, Hameed B H. The advancements in Sol–Gel method of doped-TiO2

photocatalysts. Applied Catalysis A: General., 2010, 375(1): 1–11.

[11] Chen Long-Wu, Gab Li-Hua, Xu Zi-Jie. Preparation and characterization of

monolithic TiO2 aerogels. Chemical Journal of ChineseUniversites,2001,22(11): 1916–1918.

[12] Stengl V, Bakardjieva S, Subr J, et al. Titania aerogel prepared by low

temperature supercritical drying. Microporous and Mesoporous Materials, 2006, 91(1/2/3): 1–6.

[13] Hwang S W, Kim T Y, Hyun S H. Effect of surface modification conditions on

the synthesis of mesoporous crack-free silica aerogel monoliths from waterglass via ambient-drying. Microporous and Mesoporous Materials, 2010, 130(1/2/3): 295–302.

[14] Hwang S W, Kim T Y, Hyun S H. Optimization of instantaneous solvent

exchange/surface modification process for ambient synthesis of monolithic silica aerogels. Journal of Colloid and Interface Science, 2008, 322(1): 224–230.

[15] LIU Zhao-Hui, SU Xun-Jia, HOU Gen-Liang. Effects of silicon content on

microstructure and photocatalytic activity of TiO2/SiO2 composite aerogels.

Journal of Inorganic Materials, 2010, 25(9):911–915.

[16] Hu Jie-Gang, Chen Qi-Yuan, Li Jie, et al. Preparation of TiO2 aerogels by

ambient pressure drying. Journal of Inorganic Materials,2009, 24(4): 685–689.

[17] Kucheyev S O, Baumann T F, Wang Y M, et al. Synthesis and electronic

structure of low-density monoliths of nanoporous nanocrystalline anatase TiO2.

Journal of Electron Spectroscopy and Related Phenomena., 2005, (144–147): 609–612.

[18] Cao S L, Yao N, Yeung K L. Synthesis of freestanding silica and titania-silica

aerogels with ordered and disordered mesopores. J. Sol-Gel Sci. Technol., 2008, 46(3): 323–333.

[19] Armaroli T, Milella F, Notari B. A spectroscopic study of amorphous and

crystalline, Ti-containing silica and their surface acidity. Chemistry and Materials Science., 2001, 15(1): 63–71.

议论文写作之叙例

拟题 原则： 准确、凝练 新颖、贴切 形象、优美 含蓄、醒目 形式：主谓、动宾 幻灯片2 学生拟题展示 ●态度决定人生你的不顺，正是你成长的时机 ●拥抱理性，内蕴天地逆流而上，勇往直前 ●拥抱生活无惧生活心视浮云 ●让乐观之花在生活中绽放不向风雨屈服 ●唤醒谦逊 ●心态：生活那些事 ●充满缺陷的幸福 幻灯片3 议论段写法 幻灯片4 叙例 论据的顺序安排： ●在同一篇章或同一段落内，多个论据的顺序安排一般遵循这个原则： ●古今中外 幻灯片5 议论文写作之叙例 练习：论证“失败是成功之母”该怎样叙述呢？ 化学家诺贝尔为减轻工地上挖土工人的繁重劳动，决心发明炸药。四年里，诺贝尔废寝忘食，一丝不苟做了数百次实验，换来的却只是数百次失败，但是，他毫不气馁, 因为他心中始终有一个坚定信念：一定要发明炸药，减轻工人们繁重的负担。最后一次实验时，他聚精会神地盯着延燃的导火线，一声巨响，炸药爆炸产生了极大的威力，人们在旁边不禁惊叫：“诺贝尔完了！”然而，正当人们为失去一位伟大的化学家而悲痛的时候，诺贝尔神奇般的从浓烟中跳出来，他面孔乌黑，身上带着血，兴奋地狂呼：“成功了”。就这样，诺贝尔发明了炸药，从那时起，大大减轻了挖土工人的劳动强度。

议论文写作之叙例 要点概括： 诺贝尔发明炸药的目的① 努力的经过② 最后一次试验的场面③④ 炸药的作用⑤ 我们再来看一下论点“失败是成功之母”，它具有三个要素：①经历了失败，②经过不懈努力，善于从失败中吸取经验教训，③最终取得了成功。 材料与之相关的只有②（经历了数百次失败）和⑤（最终发明了炸药）。 幻灯片7 议论文写作之叙例 问题 对策只是叙述而不描写，是择要交代梗概，舍弃其中的细节 紧扣所定论点，舍弃无关内容 理清逻辑关系，遵循古今中外 叙述的语言过于繁多，以叙代议 叙述的角度不够明确，无侧重点 叙述的事例杂乱无章，缺层次感 幻灯片8 事实论据: 摆事实举例子 主要解决三个问题： 一是叙事的繁简 二是事实论据与论点的联系 三是材料的多与少 幻灯片9 学生作文存在的毛病: 一叙述起事例来就长篇大论，时间，地点，人物，事情的起因、经过、结果全出来了，弄得文章前后像议论文，中间像记叙文，四不象！ 议论文中叙述事实:宜简不宜繁

分析文章的写作特点

分析文章的写作特点，就是分析文章如何设计主体结构、布局某篇、遣词造句。看文章的各个侧面在表现手法上有何优点，也就是看文章以怎样的形式命题，如何设计文章的情节，怎样安排文章的叙述顺序，怎样开头结尾，利用什么方式表达文章的内容，如何运用修辞标点等。具体分析方法如下： 第一．分析文章的标题。 文章的标题是文章的眼睛，它是一篇文章的重要组成部分。好标题能揭示文章的主题思想，能发人深省，引导读者理解主题。好的标题确切鲜明，富有吸引力，能给人以新鲜的感觉和深刻的印象，使人产生“急欲下读”的强烈愿望。分析文章的写作特点，首先要注意文章标题的形式及作用。 第二．分析文章的情节。 文章的情节很重要，如果把文章的主体比作“灵魂”，那么情节就是“血肉”。文章有血有肉，才有生命力。分析文章的情节是否完整，就常见的记叙文来说，就要看它任何抓住事情发生的时间、地点、人物、事情的起因、经过、结果这六个要素。如果是说明文，就看文章是否通过对实体事物的解说或对抽象事理的阐述，是人们对事物的形象、性质、功能、关系或对事理的概念、特点、来源、演变、异同等有所认识，从而或得有关知识。如果是议论文，就要看它是否具备论点、论据、和论证三要素。论点是否鲜明，论据是否确凿，论证是否合逻辑。 第三．分析文章的叙述顺序。 文章的结构完整，要求材料安排得合理，使条理清楚，脉络分明，这主要表现在文章的叙述顺序上。 1、顺叙。就是安时间的先后和事件发生、发展的顺序进行叙述。 2、倒叙。就是先写出事情的结果或发生的某一突出的片段，然后再按时间顺序对事件的发生、发展进行叙述。 3、插叙。在叙述中心事件的过程中，由于内容的需要，暂时中断，穿插一段写中心事件相关的事情，然后再转入顺叙。 第四．分析文章的开头、结尾。 好的开头，引人入胜；好的结尾，余味无穷。 开门见山，直截了当；自然收尾，干脆利落； 提出问题，吸引读者；总结全文，点明主题； 说明情况，介绍背景；照应开头，留有余味； 描写环境，引出人物；写景抒情，发人深思； 第五．分析文章的表达方式。 文章的表达方式，主要看它是采取叙述、描写，还是采取议论、抒情的方式来写作，叙述就是把人物的经历或事物发展、变化的过程直接表达出来。描写就是对人物、事件、环境等，进行生动、形象的描写和刻画，使之有形、有声、有色地再现在我们的面前，从而增强文章的生动性和感染力。描写往往和叙述结合起来使用，写人的文章，很注意人物语言、动作、心理的描写，注意周围环境的描写。抒情就是作者对所写的人物、事件抒发爱憎、好恶的感情。议论就是讲道理，作者往往是通过材料和逻辑推理，；来阐述自己的观点，表明赞成什么或反对什么。这四种表达方法也常常是在文中综合运用的。 分析文章的写作特点，还应注意到很多别的方面，段落和层次，过渡和修辞、标点等。每篇文章都有其不同的特色，只有认真分析、品味，才能对文章领会得更透。

议论文指导：议论文写作指导(一)

议论文指导：议论文写作指导(一) 议论文指导：议论文写作指导(一) 议论文开头 ——好的开头是成功的一半 开头，对于作文的成败举足轻重，考场作文，更是如此。对应试者而言，时间紧，压力大，构思要快，下笔要快，有的因为找不到恰当的切入点，打不开文思的泉眼，找不到合适的表达方式而耽误宝贵的时间，影响作文水平的发挥;对阅卷者而言，最先跃入他视野的是一篇作文的题目和开头部分，第一印象足以左右他对整篇文章的评判。所以我们如何给文章起一个好头，吸引阅卷老师的眼球，给他以强烈的理性冲击和情感震撼，就不是可有可无的了;在酷热的夏日里，在十分疲倦的工作状态下，在十分短暂的阅卷时间里，如果他把看你的文章当作清风拂面，当作赏心乐事，他的目光肯在你的作文里多驻足哪怕那么几秒钟，——那么，你至少取得了一半的成功了。 一、好的议论文开头特点 高尔基说过：“(开头)好像音乐里定调一样，全曲的音调都是它给予的，也是作者花功夫的所在。”议论文的开头要讲究“短、快、靓”。 短----简洁最好三两句成段，引入本论。 快——迅捷入题要快，最好三言两语就点明文章的基本观点或议论的话题。因为评分标准中有“中心明确”的细则。开篇确定中心，有利于阅卷者按等计分，也有利于作者展开论述，不致出现主旨不清、中途转换论题等作文大忌。

靓——精彩这也是传统文论中所说的“凤头”。精彩的开头，最突出的效果是吸引阅卷者，给阅卷者留下好的印象。文章开头要精彩，多用比喻、类比、排比等修辞引入论点，还可引述名言，讲述寓言故事导入话题。 二、议论文开头的八种方法 (一.)开门见山法。这是采用率最高的一种方法。即在文章的一开头就与全文的中心论点保持一致方向，不是亮出观点，就是导出观点。 例一：育民小学举办游泳训练班，用科学理论指导学生进行游泳训练，取得显著成绩。这，又一次极好地证明了理论对实践有指导意义这个真理。 例二：60年前的今天，鼓舞全中国人民万众一心奋起反击日寇入侵的，不是别的，正是中华民族不屈不挠的民族精神。60年后的今天，鼓舞我们在“四化”道路上高歌猛进，凭实力自立于世界民族之林的，还是中华民族不甘落后、积极进取的民族精神。由此，我大声疾呼：要大力弘扬民族精神! 例三：中学六年的学习生活，给了我许多弥足珍贵的宝贵经验和深刻教训，其中之一是：失败后要不怕失败，正视失败，不懈努力，才可反败为胜。 这种开头的好处是既简洁平实，便于掌握，又开宗明义，一语破的。 例四：社会的发展(人的情感需求)呼唤我们拆除心墙。 例五：拆除心墙要有(讲究、寻求)正确的方法。

人格心理学论文 我的人格特征分析

我的人格特征分析 人格心理学是心理学中重要的学科，虽然不是从心理学领域中分离出来，但它帮助我们解释各种心理现象和人格的发展规律，并对教育，医学多方领域有积极的影响。我从气质类型学说，卡特尔特质因素论和罗特控制点理论三方面分析了自己的人格特征，从不同角度分析了自己及日常行为，处事的方式。这对自己日后更好地工作和学习有这积极的意义。 所谓的人格就是个体在行为上的内部倾向性，表现为个体适应环境的能力，情绪，需要，动机，价值观，气质，性格等方面的整合。人格是个体在先天生物遗传素质的基础上，通过后天社会环境的相互作用而形成的相对稳定而独特的心理行为模式。广义的人格与个性同义，均指人的心理面貌，包括个性倾向性以及能力，气质和性格等方面的个性心理特征。狭义的人格指性格和气质，不包括智力。人的人格不是先天就具有的，而是以先天为基础，在后天环境的作用下发展而来的。 人格心理学的两大主要来源是心理测量运动和欧洲临床精神病学的发展。人格理论是人格心理学的核心，一方面它系统地说明或解释了各种心理现象，另一方面为我们提供了研究的框架。所以人格心理学是一门科学，重要的学科，它有利于我们充实和完备心理学的内容体系。在教育方面，教师可以根据学生不同的人格特征因材施教，健全他们的人格。在管理方面，提供了一个合理使用人才的依据，优化了群体人格特征的合理配置。而且也有助于我们了解自己的人格特征，并选择合适自己的工作。同时人格心理学也推动着医学的发展。 下面我就根据人格心理学中的一些人格理论去分析我自己的人格特征。 按照气质类型的体液说分析，我属于粘液质和抑郁质的一般混合类型。这一理论是从医学的角度探索的结果。康德认为，从心理学上看，气质首先可分为感情气质和行动气质，每一种气质又可以与生命力的兴奋和松弛相连接而进一步分为四种单纯的气质：多血质，抑郁质，粘液质，胆汁质。而我兼具粘液质和抑郁质的双重特点。粘液质的人是冷血的，他们不易冲动，具有正常的理性，情绪反应迟缓，但持久，行事比较保守与刻板。抑郁质的人大都具有沉静的特点，他们对刺激的感受不太显著，但很深入，他们对与自己有关的事物都赋予其重要性，并把注意力放在事物的困难方面，他们深思熟虑，不轻易许诺。因为我是一般混合性，所以这两种气质类型的外显表现都不是特别典型，只具有一定的相关。我在日常生活中很理性，但遇事比较消极，首先看到的都是事情的困难，往往最后都由于这种心理而放弃了自己的想法。我对情绪的体验很深，往往久久郁结于中，无法排解，这样很容易钻牛角尖，走偏激，这算是我性格中的缺陷吧。但是我行为并不刻板也不保守，具有一定的开创性，也会听取别人的意见，做决定前，我会深思熟虑，考虑全面，这算是性格中的积极因素吧。 人格心理学中，卡特尔的特质因素论也是里程碑式的理论。他认为特质是构建人格结构的基本成分，就像化学元素构成宇宙万物一样。通过研究，他找到许多人格特质，并将它们从不同角度进行了分类。首先按个体与群体的角度分为个别特质和共同特质。从层次上分为表面特质和根源特质。关于人格动力，他提出动力特质，并分为能，外能和辅助。后来卡特尔根据大量的生活记录材料，问卷材料和客观测试材料编制了著名的十六种人格因素调查表。根据十六种人格因素调查表测试结果，我十六种特质基本属于平均水平，自律性偏低，敏感性，焦虑性，稳定性偏高。我既适合交际类型工作也适合偏精确性工作，比较乐群，做事也理智不幼稚。这基本符合了我对自己的认知。卡特尔认为人格是不断发展的，但受到遗传因素的制约，遗传的天性会影响他人对他的反应，影响他本身的学习方式，也限制了环境力量对其人格的塑造。就我个人而言，我遗传了父亲敏感的特性，即使后天环境存在着影响，我也在试图改变这一特质，可是最后发现并不能起多大的作用，只能缓解，无法改变。但当一个特性处于两者之间时，便可以引导，使其往好的方向发展，或者外显行为时，会表现出

初中议论文写作指导(一、二、三)

议论文写作指导（一） 议论文的写作特点： 1、明确的目的 当我们了解生活中的某件事情、某个现象或某些问题时，总会形成自己的看法、主张和观点，把这些看法、主张和观点表达出来，并加以阐释、说明，就是议论；写成文章，就是议论文。 议论文写作的目的就是为了阐述正确的看法、主张和观点，明辨是非，议论的生命就在于此。如果对生活中某件事情、某个现象或某些问题没有自己的看法、主张和观点，就没有写议论文的必要。写了没有针对性的议论文，就是无的放矢，无病呻吟。好的议论文，不但要有明确的针对性，还应该积极倡导正确的看法、主张和观点。 2、正确的观点 观点就是我们的看法和主张。一篇议论文，只有一个主要的看法和主张，这是文章的中心论点。有的议论文还有分论点。分论点是从中心论点分解出来的，从属于中心论点，几个分论点共同论证中心论点。 观点是议论文的灵魂，一个错误的观点哪怕能够自圆其说，也是无法得到大家认可的。观点的正确与否，要看它是否符合广大群众的利益和道德标准。 议论文要能写得引人深思，发人深省，必须有深刻而有创意的观点。这里的深刻而有创意，不只是指言他人所未言，还指观点是从司空见惯的事情、现象或问题中总结出来的。 3、充实的内容 写议论文，应该注意议论文的要素，即：论点、论据、论证。要内容充实，最要注重论据和论证。 论据是用来证明论点的根据。一般是用事实、道理、定律、公式来证明论点的正确性。作为论据的事实、史实和数据，必须确凿无误，否则论点就站不住脚。此外，论据要充分，也要真实可信。 论证是运用论据证明论点的过程和方法。 有些同学写议论文，往往搭了一个架子，看起来论点、论据、论证完整，可是只有一副架子而已，好比恐龙的骨架，空空洞洞，一无所有。好的议论文，应该有具体的内容，而且是精心搭配，严密组织的。 4、清晰的逻辑 不管什么文体的文章，都要讲究逻辑的严密清晰，议论文尤其讲究。一段毫无逻辑的话，只能让人读了不知所云。逻辑的严密体现在论证上。论证要严密，无懈可击，清晰地表现在行文上，让人读了一目了然。 议论文不得胡乱说话，所以语言要求准确；同时又不必板起面孔说话，所以语言尽可能活泼一些。 议论文的结构安排： 第一种：总分式（最常见的全文结构，也称“总分总式”） 论说文的全文总体结构一般都是这种结构模式。在论说文的写作中，往往围

论文写作小助手

Word论文排版艺术及技巧--- ---本科、硕士、博士毕业论文排版必须得！！ 本帖隐藏的内容需要回复才可以浏览 本文将给你提供一些用Word进行论文排版的技巧，使你的论文排版更加方便和轻松。这些技巧不只在论文写作中可以使用，在写其他文档时也可以使用。 一、页眉页脚的制作 首先介绍一个概念：节。这里的“节”不同于论文里的章节，但概念上是相似的。节是一段连续的文档块，同节的页面拥有同样的边距、纸型或方向、打印机纸张来源、页面边框、垂直对齐方式、页眉和页脚、分栏、页码编排、行号及脚注和尾注。如果没有插入分节符，Word 默认一个文档只有一个节，所有页面都属于这个节。若想对页面设置不同的页眉页脚，必须将文档分为多个节。 论文里同一章的页面采用章标题作为页眉，不同章的页面页眉不同，这可以通过每一章作为一个节，每节独立设置页眉页脚的方法来实现。 首先介绍页眉的制作方法。在各个章节的文字都排好后，设置第一章的页眉（视图菜单→页眉和页脚）。然后跳到第一章的末尾，菜单栏上选“插入→分隔符”，分节符类型选“下一页”，不要选“连续”（除非你想第二章的标题放在第一章的文字后面而不是另起一页），若是奇偶页排版根据情况选“奇数页”或“偶数页”。这样就在光标所在的地方插入了一个分节符，分节符下面的文字属于另外一节了。 光标移到第二章，这时可以看到第二章的页眉和第一章是相同的，鼠标双击页眉Word会弹出页眉页脚工具栏，工具栏上有一个“同前”按钮（图像按钮，不是文字）， 这个按钮按下表示本节的页眉与前一节相同，我们需要的是各章的页眉互相独立，因此把这个按钮调整为“弹起”状态（与上一节相同的提示文字会消失），然后修改页眉为第二章的标题，完成后关闭工具栏。如法炮制制作其余各章的页眉。 页脚的制作方法相对比较简单。论文页面的页脚只有页码，要求从正文开始进行编号，但是，在正文前还有扉页、授权声明、中英文摘要和目录，这些页面是不需要编页码的，页码从正文第一章开始编号。首先，确认正文的第一章和目录不属于同一节。然后，光标移到第一章，点击“视图→页眉和页脚”弹出页眉页脚工具栏，切换到页脚，确保“同前”按钮处于弹起状态，插入页码，这样正文前的页面都没有页码，页码从第一章开始编号。 注： 页眉段落默认使用内置样式“页眉”，页脚使用“页脚”样式，页码使用内置字符样式“页码”。如页眉页脚的字体字号不符合要求，修改这些样式并自动更新即可，不用手动修改各章的页眉页脚。 论文里页眉使用章标题，可以采用章标题做成书签，然后在页眉交*引用的方法来维护两者的一致。 二、图表自动编号 论文写作中，图和表要求按照章节进行编号如：图1.6，表4.7，图表的自动编号可以使用Word的题注功能。Word提供图表标签和表格标签，图表也就是图的标签 操作步骤：插入菜单→引用→题注，选中图表标签，编号中可以选包含章节号，这需要章节的编号联接到一个项目标号上，参照项目编号的设置，重要的是章的编号，其它节的编号联接到上层编号，则所有的章节、图、表都可以实现自动编号。把题注中不包含标签勾上，按确定插入标签，之需要在正文中的标签前键入图就可以了。表只要在标签选择中选表格就可

2020年高考作文指导：议论文例后分析方法指津【刘希国】

2020年高考作文指导：议论文例后分析方法指津 例证法是议论文写作常用的论证方法。要想使议论文论证严谨有力，就必须对论据进行分析。有些同学写的议论文，尽管论点正确、鲜明，论据也典型、可靠，但是由于在举例之后没有进一步挖掘事例包含的事理，缺乏必要的分析，导致论点和论据联系松散，给人以罗列论据之感。所以，举例之后的分析是少不得的。下面介绍几种常用的分析论据的方法。 一、揭示实质法 这种方法，就是在列举出属性相同或相关的几个事例之后，对其进行归纳升华，点明论据所包含的道理，揭示出论据与论点之间的逻辑联系，从而深化论点。如：史学家司马光写《资治通鉴》花了19 年，相声艺术宗师侯宝林为学谐语手抄一部十多万字的《谐浪》，俄国大作家托尔斯泰写《战争与和平》花了27 年，德国著名医生欧立希连续试验 914 次，终于研制成治疗人体内锤虫和抗螺旋体病菌的新药——新胂凡纳明。这些事例充分证明了古今中外无数有成就的人之所以取得事业的成功，秘诀在于他们有恒心和毅力。(考场优秀作文《恒心和毅力是成功之本》) 这段文字中，作者在列举古今中外成功者的四个事例之后，点明了其中包含的道理，从而使中心论点“恒心和毅力是成功之本”得到了有力的论证，论据与论点联系紧密。 二、正反对比法 这种方法，所举事例形成正反对照，然后加以分析，论证观点。如：黑格尔曾经自夸德国人天生就是哲学家。然而，就是这样一个天生严谨自律的民族，却在一个狂人的引诱下，陷入了战争的渊薮。人们难以忘记60年前的那幕惨剧：生灵涂炭、妻离子散、血流成河……生者在对往事的审视中找到道德的标杆，也找到了纪念的理由。德国人用尽一切方法阻止时间淡褪那血色、稀薄那呼声——修建集中营纪念馆，全力处理战后的善后问题，还有那德国总理在犹太人纪念碑前的惊世一跪！德国人在 60 年里不断地反思，不停地纪念，终于完成了灵魂的自我救赎。德意志民族向世界展示了理性的力量，也赢得了世人的尊敬！但纪念一旦脱离理性的制约，它就会变成不可控制的魔鬼。日本在60年前那幕惨剧中同样扮演了不光彩的角色，作为亚洲地区的主要刽子手，日本犯下的罪行罄竹难书。往者已矣，大和民族的纪念却是如此这般：右翼势力大肆鼓吹“中国威胁论”，还妄图为二战罪行翻案；不顾史实修订历史教科书，文过饰非，美化侵略罪行；更有首相一年一度的靖国神社“拜鬼”……日本这种偏离理性范畴的

学术论文的特点

一、学术论文的特点 1．学术性 所谓学术是指较为专门的、有系统性的学问，学术论文是学术成果的载体，它的内容是作者在某一科学领域中对某一课题进行潜心研究而获得的结果，具有系统性和专门性，而不是点滴所得。 学术性可以体现在推翻某一学位领域中的某种陈旧的观点，提出新的见解； 可以是将分散的材料系统化，用新的观点或新的方法加以论证得出新的结论； 还可以在某个学科领域中经过自己的观察、调查、实验，有新的发现、发明或创造。 2．理论性 学术论文应具有一定的理论价值，要提示事物的本质，反映客观规律。在写作中，作者须用大量的可靠材料，运用科学的方法，对本质的东西加以剖析，对规律性的进行探讨。这就要求作者不仅要对所研究的对象有全面的认识，而且还要通过论证、阐发，将自己的发现和认识提高到理论的高度。 例:网络对人际传播的影响 3．科学性 学术论文的科学性，主要是指作者能用科学的思想方法进行论文，并得出科学的结论。它要求作者以辩证唯物主义和历史唯物主义的科学态度和方法，对待研究工作，尊重客观实际，坚持实事求是。科学性是学术论文的灵魂，没有科学性的“学术论文”是没有生命力的。 二、学术论文基本特点 ? 1.学术性。有理论价值的学术论文，要做到以下几方面： ?①提出新见解。提出前人没有提出的教育观点； ?②对某一理论进行补充或完善。在教学实践中经过自己的思考、摸索，提出有创造性的教法、学法，或者对某学科领域的专业问题有自己的独特见解； ?③对某一理论质疑，提出不同的意见和观点。 ?④全面总结前人的研究结果，丰富了该研究领域的理论知识。如文献综述也算是学术论文的一种形式。 ? 2.创造性。要想论文具有创造性，要做到： ?①要问题进行长时间的、周密细致的分析研究，从中发现别人还没有发现到、涉及到、认识到的成分，言他人所未言；

本科毕业生论文写作技巧和方法

本科毕业论文写作技巧和方法 第一部分选题 选题,简单的说就是确定自己科研的课题,解决研究什么的问题,明确研究的目标和范围。选题是进行科研的第一步,而且是十分关键的一步。 ●进入论文写作准备阶段，多数的学生往往为论文的选题犯愁。的确在准备阶段，选题十分重要。选择恰当的题目进行研究，论文的写作就会顺利一些。 ●论文题目的选择是一个从大到小、从不具体到具体的过程，应该根据自己的知识结构和兴趣，确定研究方向，考虑将来论文题目的大体方向和范围，在自己课程学习、广泛阅读和资料的积累的基础上，逐步明确具体的题目。 尽量选择应用型题目 通常人们对应用性研究的定义是比较模糊的，一般它泛指将理论应用于解决具体的问题，常将应用型研究分成理论的应用和计量应用，当然实际中，往往二者之间的界限并不十分清楚，越来越多的论文在进行分析时，将理论和计量应用融为一体。我们鼓励学生选择应用性研究作为论文的题目。 宜小题大作 论文的好坏，关键要看作者是如何在论文中支持自己的观点的。 这需要作者能够清楚定义自己所要研究的问题，研究的范围不能太宽。学术论文一般不强调研究问题的宽度，更看重的是深度，如果一篇论文涉及范围太广，作者肯定是难以做到深入的。 第二部分开题报告 一、开题报告的目的 写开题报告的目的，是要请老师和专家帮我们判断一下:这个问题有没有研究价值、这个研究方法有没有可能奏效、这个论证逻辑有没有明显缺陷。 二、开题报告的结构 就要按照“研究目的和意义”、.“文献综述和理论空间”、“基本论点和研究方法”、“资料收集方法和工作步骤”这样几个方面展开。其中，“文献综述，基本论点和研究方法”是重点，许多人往往花费大量笔墨铺陈文献综述，但一谈到自己的研究方法时便寥寥数语、一掠而过。 1 选题的目的和意义 2 与主题相关的文献综述 2.1 相关的研究文献回顾 2.2 对现有文献的简要评价 3 逻辑思路与研究方法 4 论文结构与内容安排 5 可能的创新之处 6.已有的研究基础 7.主要参考文献 三、课题研究的方法 具体的研究方法可从下面选定：观察法、调查法、实验法、经验总结法、个案法、比较研究法、文献资料法等。

信息源特点分析论文

所谓信息源就是是信息的源头。信息源是从信息系统的角度对信息进行的描述。根据信息源具有共享性和再生性的特点，在一定的条件下，信息源可以转化为信息资源。为了有效地开发利用信息资源，应当加强对信息源及其分布规律的研究。分析企业信息源是进行信息资源建设的重要步骤，其目的在于明确数据收集的方向。根据不同的分类标准，可以将信息源划分为不同的类型。 1、以企业边界为界限，可以将信息源分为内部信息源和外部信息源。 内部信息源产生企业的内部信息，包括企业各个部门，如生产部、人事部等，这些部门在工作中形成大量有用信息，供管理人员分析企业当前状况，以辅助决策。同时，不同层次的管理人员依赖于其他层次的管理人员提供信息，因而他们也是内部信息源的组成部分，如中层管理者要为高层管理者提供信息，而基层管理者要为中层管理者提供信息。中层管理者还要起到上传下达的作用，将基层的情况通报给高层管理者，将上层的指示传达给基层。由此可见，企业成员本身是一种重要的信息源。 外部信息源是指在企业外部为企业活动提供信息的信息源，与企业自身的业务和外部环境密切相关。企业的外部信息源包括政府部门、司法部门和与其有关的其它社会组织。 2、根据信息是否数字化，可以将信息源分为数字化信息源和非数字化信息源。 数字化信息源提供的信息来自于计算机存储设备，包括内存和外存，并且可以通过网络传输。这类信息源包括企业内的信息系统，如TPS、MIS、DSS、Intranet、Internet 及各类检索网络等。由于有些数据和信息，如关于生产及实物处理信息通过计算机更易于存储处理和提供利用，因此人们通过一定的方式存入计算机，形成了数字化信息源。对于不同管理层次来说，不同管理层的人员对数字化信息源的利用程度不同。 .非数字化信息同样具有重要意义。企业不同层次的管理人员对非数字化信息源也有不同程度的需求。企业内部的非数字化信息源除了包括专业书籍、期刊、文书、档案等印刷型的文献以外，还包括直接观察，如管理人员到车间巡视，了解企业生产情况；企业内部的生产快报；手工收集的信息；非正式的传播渠道，如参加各种社交活动，与下属交谈等，都可能获取与企业活动相关的重要信息。企业外部的非数字化信息源分布广泛，包括专业书籍和期刊及其出版部门，大众传播媒介等，尤其在提倡知识管理的时代，部分显性知识可以存储在计算机中，而隐性知识则大部分存储在人脑中，在成为显性知识之前难以将其数字化。挖掘这类信息，对企业的发展和创新具有重要意义。因此在信息社会里，仍然要对非数字化信息源加强研究和利用。3、根据信息的载体，可以将信息源分为印刷型、缩微型、电子型、实物、声像信息源等。 4、根据信息的运动形式，可以将信息源分为静态和动态的信息源。 静态信息源提供变化不大或者不会发生变化的信息，如企业中的工资管理系统提供的信息在一定时期内不会有太大的变化，档案信息记录的是过去的事件，其信息内容一般不会发生变化，两者都属于静态信息源。动态信息源提供的信息通常处于变化中，如证券公司提供的某股票的价格信息经常在一天之内发生数次变动，再如市场需求信息常因地因人（顾客群）而表现出不同特性。因此，证券公司和市场等机构属于动态信息源。通常地，静态信息源多在企业内部，动态信息源多在企业外部。 此外，根据提供信息的单位的性质，可以将信息源分为文献信息部门和非文献信息部门，前者如图书馆、科技信息中心、档案馆，后者如与本企业有相同业务地竞争对手、咨询公司等。 一般而言，相对于特定信息需求的信息源的分布也是不平衡的，能满足用户主要信息需求的信息源大约集中在少数相关的部门中，而那些满足用户一般信息需求的信息源则分散在众多的部门中。为此，企业信息管理师要结合信息源和用户的信息需求进行交叉分析，以期发现对应于特定用户信息需求的信息源分布格局，这也是信息源分析的主要目的。

东财《论文写作指导》在线作业(随机全部答案)

1、知识点1：下面哪一描述最好的概括了毕业论文的含义？（） A、毕业论文是高等院校应届毕业生在教师指导下按学术论文标准独立完成的具有一定学术价值和应用价值的文章 B、毕业论文是一种由高等院校应届毕业生自发完成的，旨在向社会或他人提供新知识的学术论文 C、毕业论文是由高等院校应届毕业生在教师指导下对本科阶段专业知识学习情况的全面回顾、检查和分析的一种学术论文 D、毕业论文是对某一学科或领域内较为成熟的理论与知识的系统阐述，内容较为全面综合，体系框架较为庞大的一种学术文章 2、知识点1：毕业论文属于下述哪种文体?（） A、说明文 B、议论文 C、记叙文 D、研究报告 3、知识点1：毕业论文作为一种学术论文，其重要要应用在于（）。 A、记录和储存科学研究成果 B、通过交流，促进学科建设与发展 C、对学生学习情况进行考核 D、传播学术信息 4、知识点1：毕业论文写作的意义在于（）。 A、检验本科阶段学习情况 B、培养和提高学生分析能力、理论应用能力 C、提高写作水平和文字表达能力 D、为政府及投资者提供决策参考 5、知识点1：毕业论文写作仅是对本科教学阶段所学相关专业基础理论、知识和基本技能的一次全面考核。 A、正确 B、错误 6、知识点1：撰写毕业论文可以有效提高学生获取信息资料的能力、语言和文字表达能力。 A、正确 B、错误 7、知识点2：下述哪项不是毕业论文写作的基本原则。（） A、创新性原则 B、学术性原则 C、应用性原则 D、平易性原则 8、知识点2：毕业论文中的下述表述，“一个广为流传但未经证实的说法是，在中国，生活被房贷按揭所改变的青年，有2600万。”此类表述违背了毕业论文写作的哪一原则（）。 A、创新性原则 B、学术性原则 C、科学性原则 D、平易性原则 9、知识点2：毕业论文所遵循的学术性原则，具体表现在（）。

语文高考作文指导：议论文例后分析方法指津

语文高考作文指导：议论文例后分析方法指津 例证法是议论文写作常用的论证方法。要想使议论文论证严谨有力，就必须对论据进行分析。有些同学写的议论文，尽管论点正确、鲜明，论据也典型、可靠，但是由于在举例之后没有进一步挖掘事例包含的事理，缺乏必要的分析，导致论点和论据联系松散，给人以罗列论据之感。所以，举例之后的分析是少不得的。 下面介绍几种常用的分析论据的方法。 一、揭示实质法 这种方法，就是在列举出属性相同或相关的几个事例之后，对其进行归纳升华，点明论据所包含的道理，揭示出论据与论点之间的逻辑联系，从而深化论点。如：史学家司马光写《资治通鉴》花了19 年，相声艺术宗师侯宝林为学谐语手抄一部十多万字的《谐浪》，俄国大作家托尔斯泰写《战争与和平》花了27 年，德国著名医生欧立希连续试验914 次，终于研制成治疗人体内锤虫和抗螺旋体病菌的新药——新胂凡纳明。这些事例充分证明了古今中外无数有成就的人之所以取得事业的成功，秘诀在于他们有恒心和毅力。(考场优秀作文《恒心和毅力是成功之本》) 这段文字中，作者在列举古今中外成功者的四个事例之后，点明了其中包含的道理，从而使中心论点“恒心和毅力是成功之本”得到了有力的论证，论据与论点联系紧密。 二、正反对比法 这种方法，所举事例形成正反对照，然后加以分析，论证观点。如： 黑格尔曾经自夸德国人天生就是哲学家。然而，就是这样一个天生严谨自律的民族，却在一个狂人的引诱下，陷入了战争的渊薮。人们难以忘记60年前的那幕惨剧：生灵涂炭、妻离子散、血流成河……生者在对往事的审视中找到道德的标杆，也找到了纪念的理由。德国人用尽一切方法阻止时间淡褪那血色、稀薄那呼声——修建集中营纪念馆，全力处理战后的善后问题，还有那德国总理在犹太人纪念碑前的惊世一跪!德国人在60 年里不断地反思，不停地纪念，终于完成了灵魂的自我救赎。德意志民族向世界展示了理性的力量，也赢得了世人的尊敬! 但纪念一旦脱离理性的制约，它就会变成不可控制的魔鬼。日本在60年前那幕惨剧中同样扮演了不光彩的角色，作为亚洲地区的主要刽子手，日本犯下的罪行罄竹难书。往者

学术论文写作教学大纲

《学术论文写作》教学大纲 一、课程说明 1. 课程代码：1 2. 课程中文名称：学术论文写作 3. 课程英文名称：Academic Thesis Writing 4. 课程总学时数：16 5. 课程学分数：1 6. 授课对象：英语专业四年级学生 7. 本课程的性质、地位和作用 本课程是《高等学校英语专业英语教学大纲》中规定的必修课，也是我院针对英语专业四年级学生开设的一门专业选修课，在学科体系中居重要地位。本课程有利于培养学生进行科学研究的能力，并帮助、指导学生顺利完成毕业论文写作。毕业论文写作是大学英语专业教学计划中一个不可缺少的部分和实践环节，是考查学生综合能力、评估学业成绩的一个重要方式，是高校英语专业教学质量评估的重要内容。毕业论文写作的优劣决定学生毕业时可否被授予学士学位。本课程可以培养学生的科研创新意识、严谨工作态度，良好学术道德，锻炼学生的思维组织能力，训练学生的语言运用能力，激活学生的知识输出与输入。通过教学，使学生了解毕业论文的写作要求和撰写规范，知道，并掌握写作论文的方法。 二、教学基本要求 1. 本课程的目的、任务 本课程的教学目的在于培养学生撰写毕业论文的能力，要求学生对文献材料有一定的综合分析能力、并能用自己的语言表达个人观点和意见，同时还要求学生学会正确地引用他人的观点，避免有意或无意的抄袭现象。本课程的任务是使学生了解从选题、文献调研、资料分析、列提纲、起草、修改到编辑的写作基本方法和基本技能，了解毕业论文开题报告、文献综述、摘要、引言、正文、结语的写作方法及文献引用方法等，为学生毕业论文写作提供指导和帮助，对学生进行基本的科研能力训练，培养学生的创新意识及独立思维、科学探索的能力。

论文写作技巧

论文写作技巧 当我们对一个问题研究之后,如何将其展现于众人面前是一个重要的工作.在这里我们结合具体的事例,给大家介绍科研的一个重要部分枣论文的一般格式及其注意事项.当然,要写出一篇好的论文,绝不是单单这么一个简要的介绍就够了,还需自己多写,多练. 随着科学技术的发展,越来越多的学者涉及到学术论文的写作领域,那么怎样写学术论文,学术论文写作是怎样要求的,格式如何,下面就介绍一下学术论文的写作,希望能对您论文写作有所帮助. (一)题名(title,topic) 题名又称题目或标题.题名是以最恰当,最简明的词语反映论文中最重要的特定内容的逻辑组合. 论文题目是一篇论文给出的涉及论文范围与水平的第一个重要信息,也是必须考虑到有助于选定关键词不达意和编制题录,索引等二次文献可以提供检索的特定实用信息. 论文题目十分重要,必须用心斟酌选定.有人描述其重要性,用了下面的一句话:论文题目是文章的一半. 对论文题目的要求是:准确得体:简短精炼:外延和内涵恰如其分:醒目. 对这四方面的要求分述如下. 1.准确得体 要求论文题目能准确表达论文内容,恰当反映所研究的范围和深度. 常见毛病是:过于笼统,题不扣文.关键问题在于题目要紧扣论文内容,或论文内容民论文题目要互相匹配,紧扣,即题要扣文,文也要扣题.这是撰写论文的基本准则. 2.简短精炼 力求题目的字数要少,用词需要精选.至于多少字算是合乎要求,并无统一的硬性规定,一般希望一篇论文题目不要超出20个字,不过,不能由于一味追求字数少而影响题目对内容的恰当反映,在遇到两者确有矛盾时,宁可多用几个字也要力求表达明确. 若简短题名不足以显示论文内容或反映出属于系列研究的性质,则可利用正,副标题的方法解决,以加副

学术论文写作的要点

一、研究生必备四本 俗话说好记性不如烂笔头，所以一定要首先养成做笔记的好习惯！作为研究生下面这几个本子是必不可少的。 1，实验记录本（包括试验准备本），这当然首当其冲必不可少，我就不多说了； 2，Idea记录本，每次看文献对自己有用的东西先记下，由此产生的idea更不能放过，这可是做研究的本钱，好记性不如烂笔头，以后翻翻会更有想法的； 3，专业概念以及理论进展记录本，每个人不可能对自己领域的概念都了如指掌，初入门者更是如此，这时候小小一个本子的作用就大了； 4，讲座记录本，这本本子可能有些零杂，记录听到的内容，更要记录瞬间的灵感，以及不懂的地方，不可小视！ 这四本是你必不可少的，不过作为我们这些非英语专业的研究生来说，还有一个应该具备的本子就是英语好句记录本。 二、论文写作要点 1、选题要小，开掘要深；不要题目很大，内容却很单薄。 2、写作前要读好书、翻阅大量资料、注意学术积累，在这个过程中，还要注重利用网络，特别是一些专业数据库 3、“选题新、方法新、资料新”的三新原则（老板教导的） 4、“新题新做”和“小题大做 总之，一点之见即成文。 三、如何撰写实验研究论文（唐朝枢） 论文发表意识：基础研究成果的表达方式；是否急于发表（创新与严谨的关系）；发表的论文与学位论文的区别（反映科学事实而不是反映作者水平） 论文格式：原著 original research paper, full length paper、review综述论文，快报、简报、摘要。不同于教科书、讲义，更不同于工作总结。 撰写前的准备工作：复习和准备好相关文献;再次审定实验目的(学术思想,Idea);实验资料完整并再次审核 1.Introduction:引言 问题的提出；研究的现状及背景；以前工作基础；本工作的目的；思路（可提假说）；对象；方法；结果。在…模型上，观察…指标，以探讨…（目的）

初中语文_议论文写作之例后分析 教学设计学情分析教材分析课后反思

议论文写作之例后分析 ——初三议论文写作研讨课一、导入： 采访一下：愿写作文吗？愿意。师：那你肯定是一个善于观察、留心生活的孩子，今天的学习会助你写作的一臂之力的； 生：不愿。老师告诉你：不愿写作文是不行的，因为作文是你语文学习的半壁江山；（如果素材匮乏，语文离不开生活，多走近生活，有素材了；如果语言功底不行，那就多背好的片段，没有捷径可走的。） 但学习议论文写作后，你就会愿意写作了，而且特别愿意写议论文了，可能不久你会爱上议论文写作了。一是好写，因为议论文相对有结构可循的，二是中高考的高分或满分作文多数是议论文，特别是高考满分作文基本都是议论文，所以议论文不仅好写，而且掌握了技巧方法，你还会得高分呢？所以要增强信心哦。 在学习之前我们先回忆一下有关议论文的知识。 二、回顾知识： 1、你都了解了议论文哪些知识?做（导学案）题并记下来： 1、判断题：①议论文是以议论为主要表达方式，通过摆事实、讲道理，直接表达作者的观点和主张的常用文体。 （）②议论文是以理服人，记叙文是以情感人，说明文是以知授人。（）③议论文的基本要素有：论点、论据、论证。论点和论据之间的关系是证明与被证明的关系。论点是解决“需要证明什么,”论据是解决“用什么来证明”,论证是解决“怎样证明”.（）④议论文的一般结构是：提出问题（引论），分析问题（本论），解决问题（结论）。 2、填空题： ①议论文最基本的论证方法、 ②论据分为（代表性的事例，确凿的数据，可靠的史实等）和 （名言警句、谚语格言以及作者的说理分析） ③论证方法及其作用 1、举例论证(摆事实)：运用具体事例，真实可信，增强文章说服力，趣味性，权威性，让文章浅显易懂 2、道理论证(讲道理)：增强文章说服力或文采，使论证更有力或更深入。 3、比喻论证(讲道理)：形象生动地阐述了某一论点，使说理更通俗易懂。 4、正反对比论证(讲道理)：通过对比，突出强调了某一论点，使说理更鲜明。过渡语：

冰心文章特点分析

冰心文章特点分析 冰心文章的特点从4个方面分析，如下： 一、小说 冰心在刻画人物形象时，大多不用浓墨重彩，也较少精雕细刻，只用素描的笔法，淡淡数笔，人物形象就仿佛那出水的芙蓉，鲜灵灵地浮现在水面上。《六一姐》、《冬儿姑娘》、《小桔灯》分别塑造了三个生活在不同时代的少女形象。冰心在小说中塑造了一系列理想、完美的青年女性的形象。她们大多心地善良，温柔美丽，活泼大方，稳健端庄。她们青春焕发，充满活力，以自己的智慧和才能，赢得女性的尊严；以自身事业上的辉煌成就，获得男人的敬重。此外还有一系列热爱祖国的青年，慈怜温柔的伟大母亲，通情达理的老奶奶，以及博学风趣的老教授等众多形象，透出了温情。 在艺术表现上，冰心善于借鉴和运用抒情手法。在作品中，时而以叙述人的口吻直接抒发情感，时而通过人物的语言或人物的心理活动来表露作者的主观意态，使小说带着浓重的抒情色彩。 冰心往往喜欢用第一人称的叙事手法。以“我”作为展开故事的线索，满蕴着深情，倾诉我的所见、所闻、所遭、所感、所触，使读者感到小说中所发生的一切，全是人生的真实，没有虚构编织的成分，没有浪漫的色彩，没有人为的戏剧性的冲突，没有媚俗的诙谐，具有逼真性和亲切感。这给作者提供了更大的自由，可以更灵活地起讫，转折，变化，作者浓烈的情愫的抒发，可以表达得更加得心应手。 冰心的小说，较少宏篇巨著，多是清新隽永的珍品。她的许多作

品看起来情节单纯，却寓意深远，留给人无穷的回味。她撷取现实生活中的一个片段，人生旅途中的一段机缘，展示出错综复杂的社会生活的一个侧面。没有离奇曲折的故事，没有金戈铁马的壮举，却具有一种哲理的追求。她常常用机敏的目光，去观察社会，审视人生；从人际关系撞击中，爆发出火花，捕捉生活中蕴藏的哲理，寄托自己的情思，富有清新的哲理和诗意。 在小说的结构上，大多采用双向型的结构框架，互相映照的格式。她常以两个家庭、两个人物、两个事件，大洋两岸为主线，平衡展开，发展的结局，却是大相径庭的。通过鲜明的对比，给人们以启迪，发人深思。在小说的描写手法上，她常采用白描的手法，以简练的笔墨，不加烘托，勾勒出鲜明的形象，表现她特有的诗的情性。 冰心的作品，往往把人物活动的时间安排在清晨、黄昏、月夜；活动的场景设置在海滨、湖畔、公园、山间、船上；借助自然景物的描摹，将人物的美与环境的美，融为一体，达到情景交融的境地，造成特定的温馨的氛围。 二、散文 冰心的散文，题材广泛，寓意深邃。冰心通过自身经历的细腻描写，生动而形象地反映了一个世纪来，中国动荡复杂的社会生活的某些侧面。在冰心的散文里可以看到在半殖民地半封建的旧中国，帝国主义、封建主义、官僚买办阶级压迫蹂躏中国人民的惨景，以及英雄人民、爱国青年奋起反抗，英勇斗争的画面。同时，冰心的散文题材还扩展到世界上许多国家的历史、地理、文化、风俗，以及人民群众

2021年学术论文写作技巧

第一条，先要围绕着论题去占有和选择材料。 也就是说，当你的论题已经确定以后，第一，围绕着立论去占有材料，多多益善的去看。有的论题是来自老师已经拟订好的题目。有相当一部分学生是自己确立论题的，先积累材料，再有论点。一旦立论确立了以后，再回过头来去占有材料。在占有材料方面跟我《基础写作》里讲的有相通的地方。第一要占有材料，占有研究对象的真实的材料。比如你要研究某个作家，某个阶段的几部作品，就将这几部作品拿来进行深入细致的研读，进一步来确定自己的论点。如果你的论文是报告类的，不是纯理论性的，用实验报告、调查报告、总结的形式来写论文的，那么你的调查材料、实验材料也要占有。 第二，要对研究对象的外延材料占有。 比如你要研究的是作家作品的话，那么你就要对作家写作的背景材料，包括政治经济背景、文艺思潮背景等。还有作家谈自己创作的材料，还有他人已经研究过的材料等。有了这些材料，你就可以做到知人论世，可以使自己在研究当中尽量公允，不带偏见。所以，充分占有材料，也就使你的论据更充分。这样你将来的论证就会更加深广。 第三，在有材料的基础上要选择材料。 决不能只要有材料就统统拉进来。这是你们写论文常出现的问题。比如让你写一万字，你可能写到五六万字。象刚才那个学生一样，写出六万字，太丰富了。把握不住自己的时候，可以让老师来帮助你，告诉你哪些能用，哪些不能用。多占有材料总比没有材料写不出来要好，因为删总是好删的。在材料多的情况下，你就选更好的材料。 2 、选择论文的类型。 第二项准备工作就是选择论文的类型。毕业论文的类型一是学术性论文，二是报告性论文。应用性比较少的科目来说比较容易做成学术型论文，比如对作家、作品的研究，对诗派的研究。应用性比较强的学科，比如教学领域、新闻领域、治疗科学和实验等，论文一般写成调查性的或总结性的，我将它概括为报告型论文。 杂志上发表的3来字的论文，一般就是报告型的论文。报告型的论文主要是总结经验。不管是总结也好，报告也好，总之，最后是要总结出规律性的东西来。比如说，《新教材综合性学习的教学体会》有这样几条规律综合性学习能够激发学生积极参与和主动学习;综合性学习能够激发学生的创造意识，培养学生的创造能力;综合性学习以课外学习为主，能加强课内外的结合，强化能力的培养;综合性学习能强化学生对语文学习的体验和认识，使学生的情感态度和价值取向朝着健康的方向发展。他的这几个体会是努力地从理论上探讨，说明它的意义。 大多数学生的论文都是学术型的，学术型的论文主要是对某一个专业领域的问题，经过充分的研究以后，用文字符号进行表达。这一类论文的基本要求是论者以自己所学的知识，对本专业的理论问题或实际问题进行探讨和研究。学术型的论文还可以细分为两种，一是论述性的论文，一是综述性的论文。所谓论述性的论文，最大的特点是以议论为主，有极强的理论色彩。它又可以分为立论型和驳论型。立论型就是正面树立自己的观点，驳论型就是批驳别人的观点。综述性的论文，在我们的大型报纸上和一些杂志很多。比如，XX年已经过了半年了，我们就可以