ASTM A350LF2 化学成分表

Quality ASTM A 350 LF2

According to standards ASTM A 350M – 07 Lucefin Group Number --

Chemical composition

C% max Si% Mn% P%

max

S%

max

Cu%

max

Ni%

max

Cr%

max

Mo%

max

V%

max

Nb%

max

0,30 0,15-0,30 0,60-1,35 0,035 0,040 0,40 0,40 0,30 0,12 0,08 0,02

The sum of copper (Cu), chromium (Cr) and molybdenum (Mo) shall not exceed 1,00% The sum of chromium (Cr) and molybdenum (Mo) shall not exceed 0,32%

Carbon Equivalent CE = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/ 15 max 0,47

Temperature °C

Hot forming Normalizing Quenching Tempering Stress relieving

1150-850 880-930

air cooling 880-930

oil / polymer water

590

air cooling

50 under the temperature of

tempering

Soft annealing Normalizing

and Tempering

Isothermal

annealing

Preheating

welding

Stress relieving

after welding (PWHT)

200 590 furnace cooling

A C1 A C3M S Mf

700

air cooling 900 air

600 air

860 furnace

cooling to

660 after, air -- -- ----

Mechanical properties Steel Forgings

make reference the values of Forgeds Heat treatments must grant below mentioned values ASTM A 350M - 07

Testing at room temperature (longitudinal)

all dimension

mm R Rp 0.2A% C% - Z%Kv –46 °C cl. 1Kv –18 °C cl. 2HB N/mm2N/mm2 min. min. min. J average / minimum max

-- T 485-655 250 22 30 20 / 16 27 / 20 197

T= is the maximum heat-treated thickness

test specimen shall correspond to the ? T

Testing ( longitudinal ) LUCEFIN esperience

R Rp0.2 A C - Z Kv - 46 °C Kv - 18 °C product Heat treatments ? product

mm N/mm2N/mm2% % J J

Quenching 880 °C water

Tempering 640 °C air

95 600 480 24.6 58.0 68-66-64 112–114-110 Hot-rolled Normalizing 900 °C air 210 580 400 32.6 64.4 22–24-18 70–74-70 Hot-rolled Natural -- 95 526 302 28.6 62.0 6-6-4 16-10-8 Hot-rolled EUROPE EN ITALY UNI CHINA GERMANY DIN FRANCE AFNOR U.K. B.S. RUSSIA USA AISI/SAE

S355J2G3 appr. Fe510 appr. 16Mn St52.3 N -- 50D 20G A350 LF2 cl. 1 – cl. 2

常用不锈钢化学成分.

常用不锈钢化学成分 钢号国内号 各化学成分含量（%） C Cr Ni Ti Mn Si S Mo P Al Cu Fe 3040Cr19Ni9≤0.0818.0～20.08.0～10.5——≤2.00≤1.00≤0.030≤0.045————余量304L00Cr19Ni11≤0.0318.0～20.09.0～13.0——≤2.00≤1.00≤0.030≤0.045余量309S0Cr23Ni13≤0.0822.0～24.012.0～15.0——≤2.00≤1.00≤0.030≤0.035————余量3160Cr17Ni12Mo2≤0.0816.0～18.010.0～14.0——≤2.00≤1.00≤0.030 2.0～3.0≤0.045————余量316L00Cr17Ni14Mo2≤0.0316.0～18.012.0～15.0——≤2.00≤1.00≤0.030 2.0～3.0≤0.045————余量3211Cr18Ni9Ti≤0.1217.0～19.08.00～11.0≥5×C≤2.00≤1.00≤0.030≤0.035————余量322≤0.1216.0～18.0 6.00～8.00 1.00≤2.00≤1.00≤0.030≤0.045 1.00——余量332≤0.0819.0～23.030.0～40.0≤0.60≤2.00≤0.75≤0.030≤0.040≤0.60——余量4301Cr17≤0.1216.0～18.0≤0.60——≤1.00≤0.75≤0.030≤0.035——余量430LX1Cr17(铁素体)≤0.0316.0～19.0≤0.600.1～1.0≤1.00≤0.75≤0.030≤0.040——余量英格莱600≤0.1514.0～17.0≥72.0——≤1.00≤0.50≤0.015————≤0.506～10英格莱801≤0.0520.5032.0 1.10——————————0.15余量英格莱8250Cr21Ni42Mo3Cu2Ti≤0.0219.5～23.538.0～46.00.6～1.2≤1.00≤0.50≤0.030 2.5～3.5——≤0.20 1.5～3.022.0min 英格莱840≤0.0818.0～22.018.0～22.0—— 1.00 1.00————≤0.60——余量334≤0.0818.0～22.018.0～22.0≤0.60≤2.00≤0.75≤0.030≤0.040≤0.60——余量NAS840≤0.0818.0～22.018.0～22.0≤0.60余量310S0Cr25Ni20≤0.0824.0～26.019.0～22.0——≤2.00≤1.50≤0.030≤0.045————余量840REP≤0.0824.0～26.019.0～22.0——余量英格莱8001Cr21Ni33AlTi≤0.1019.0～23.030.0～35.00.40≤1.50≤1.00≤0.015——0.15～0.6≤0.7539.5min NAS800≤0.1019.0～23.030.0～35.00.15～0.6余量钢号国内号C Cr Ni Ti Mn Si S Mo P Al Cu Fe 注：钢号是美国命名法 各成分作用：C含量增加，合金硬度和耐磨性都增大，而塑性跟韧性减小； Si抗氧化；Mn在奥氏体中可耐磨，韧性好；P、S为有害杂质，P冷脆，S热脆； Cr、Ni、Mo具有抗蚀性，Ni只有与Cr一起才起作用；Al抗氧化；Cu耐蚀。

304不锈钢规格表

304 不锈钢板规格表产品材 质： 1：200 系列（铬-镍-锰奥氏体不锈钢）主要有： 2 01、2022： 300 系列（铬-镍奥氏体不锈钢）主要有： 3 01、3 02、3 03、303CU、 304、304L、304 F、304H、 310、310S、 314、314L、 316、316L/321 不锈钢板面宽度： 2000mm 不锈钢板厚1000mm、1220mm、1250mm、1500mm、1800mm、 度： 0. 1、0.2/ 0.3/ 0.5/

0.6/ 0.7/ 0.8/ 0.9/ 1.0/ 1.5、 2.0/ 2.5/ 3.0/ 4.0/ 5.0/ 6.0/ 8.0/9/10/12/16/18/20/22/25/30mm 不锈钢板理论重量计算公式： 长*宽*厚度*密度=重量/公斤不锈钢管计算公式： 直径-壁厚*壁厚* 0.02491=1米重量/公斤不锈钢板厚度标准@不锈钢板标准厚度冷轧部：不锈钢板冷轧2B(卷板、卷带、平板)特色板： 3. 5mm—6mm 304/2B，316L/2B 厚度： 冷扎2B( 0.1— 6.0mm)；表面：

2B光面、BA；8K镜面；拉丝、磨砂；雪花砂；不锈钢无指纹板；装饰面板： 彩色板、镀钛板、蚀刻板、油抛发纹板（HL、NO.4）、3D 立体板、喷砂板、压纹板热轧部： 不锈钢板热轧No.1（卷板、平板）厚度： 工业No.1（ 3-159mm ）表面： 8K镜面；拉丝、磨砂；雪花砂；不锈钢无指纹板；特别加工： 可按客户指定开不定尺寸不锈钢管材质： 201 不锈钢管202不锈钢管301不锈钢板管304不锈钢管321 不锈钢板管316 不锈钢板管310S管不锈钢管材系统： （不锈钢管、不锈钢无缝管、不锈钢装饰管、不锈钢有缝管、不锈钢卫生管、不锈钢精密管、不锈钢毛细管）不锈钢板厚度标准@不锈钢板标准厚度表面有： 工业面、普通抛光面、镜面、拉丝面、、、、、① 不锈钢管圆管规格表：不锈钢板厚度标准@不锈钢板标准厚度Φ3Φ4Φ5Φ6Φ7Φ8Φ 9.5 Φ 10Φ 12.7 Φ 15.9 Φ 19.1 Φ 22.2 Φ 25.4 Φ 31.8 Φ 38.1 Φ 42.16 Φ 50.8 Φ

常用钢板厚度规格大全

钢板是钢材四大品种（板、管、型、丝）之一，在发达国家，钢板产量占钢材生产总量50％以上，随着我国国民经济的发展，钢板生产量逐渐增长。钢板是一种宽厚比和表面积都很大的扁平钢材。钢板按厚度分为薄板和厚板两大规格。薄钢板是用热轧或冷轧方法生产的厚度在之间的钢板。薄钢板宽度在500-1400mm之间。根据不同的用途，薄钢板采用不同材质钢坯轧制而成。通常采用材质有普碳钢、优碳钢、合金结构钢、碳素工具钢、不锈钢、弹簧钢和电工用硅钢等。它们主要用于汽车工业、航空工业、搪瓷工业、电气工业、机械工业等部门。薄钢板除轧制后直接交货之外，还有经过酸洗的、镀锌和镀锡等种类。厚钢板是厚度在4mm以上的钢板的统称，在实际工作中，常将厚度小于20mm的钢板称为中板，厚度＞20mm至60mm的钢板称为厚板，厚度＞ 60mm的钢板则需在专门的特厚板轧机上轧制，故称特厚板。厚钢板的宽度从。厚板按用途又分造船钢板、桥梁钢板、锅炉钢板、高压容器钢板、花纹钢板、汽车钢板、装甲钢板和复合钢板等。钢板的一个分支是钢带，钢带实际上是很长的薄板，宽度比较小，常成卷供应，也称为带钢。钢带常在多机架连续式轧机上生产，切成定尺长度后就是钢带，因此生产率比单张机制时高。一、中、厚板（一）普通中、厚钢板 1、普碳钢沸腾钢板（GB3274-88）普碳钢沸腾钢板顾名思义是由普通碳素结构钢的沸腾钢热轧制成的钢板。沸腾钢是一种脱氧不完全的钢材，钢液含氧量较高，当钢水注入钢锭模后，碳氧反应产生大量气体，造成钢液呈沸腾状态而得名。沸腾钢含碳量低，且由于不用硅铁脱氧，故钢中含硅量常＜%。沸腾钢

的外层是在沸腾状态下结晶的，所以表层纯净、致密，表面质量好，加工性能良好。沸腾钢没有大的集中缩孔，用脱氧剂少，钢材成本低。沸腾钢心部杂质多，偏析较严重，力学性能不均匀，钢中气体含量较多，韧性低、冷脆和时效敏感性较大，焊接性能较差，故不适用于制造承受冲击截荷，在低温下工作的焊接结构件和其他重要结构件。（1）主要用途沸腾钢板大量用制造各种冲压件、建筑及工程结构和一些不太重要的机器结构和零件。（2）材质的牌号、化学成分和力学性能符合GB700-79(88)(普通碳素结构钢技术条件)中沸腾钢的规定。参阅（型钢）等部分。（3）钢板规格尺寸热轧厚钢板厚度为。（4）生产单位普碳沸腾钢板由鞍钢、武钢、马钢、太钢、重庆钢厂、邯郸钢铁总厂、新余钢厂、柳州钢厂、安阳钢钢公司、营口中板厂和天津钢厂等生产。 2、普碳钢镇静钢板（GB3274-88）普碳镇静钢钢板是由普通碳素结构钢镇静钢坯热轧制成的钢板。镇静钢是脱氧完全的钢，钢液在注锭前用锰铁、硅铁和铝等进行充分脱氧，钢液在钢锭模中较平静，不产生沸腾状态，故得名为镇静钢。镇静钢的优点是化学成分均匀，所以各部分的机械性能也均匀，焊接性能和塑性良好、抗腐蚀性较强。但表面质量较差，有集中缩孔，成本也较高。（1）主要用途普通镇静钢板主要用于生产在低温下承受冲击的构件、焊接结构及其他要求较高强度的结构件。（2）材质的牌号、化学成分和力学性能符合GB700-79(88)（普通碳素结构钢技术条件）中镇静钢的规定。参阅型钢等部分。（3）钢板规格尺寸热轧厚板厚度。（4）生产单位普碳镇静钢板由鞍钢、武钢、舞阳钢铁公司、马钢、太钢、

不锈钢常见钢种及化学成分

不锈钢化学成分 组织类型序 号 级别UNS编号 化学成分（质量分数）/% C Mn P S Si Cr Ni Mo N B Nb Ti 其他 元素 奥氏体不锈钢1TP304S304000.08 2.000.0450.030 1.0018.0-20.08.0-11.0……….……2TP304H S304090.04-0.10 2.000.0450.030 1.0018.0-20.08.0-11.0……………3TP304L S304030.035D 2.000.0450.030 1.0018.0-20.08.0-13.0……………4TP310S S310080.08 2.000.0450.030 1.0024.0-26.019.0-22.00.75 5TP316S316000.08 2.000.0450.030 1.0016.0-18.011.0-14.0E 2.00-3.00…………6TP316L S316030.035D 2.000.0450.030 1.0016.0-18.010.0-14.0 2.00-3.00…………7TP316H S316090.04-0.10 2.000.0450.030 1.0016.0-18.011.0-14.0E 2.00-3.00…………8TP316Ti S316350.08 2.000.0450.0300.7516.0-18.010.0-12.0 2.00-3.000.10…5x(C+N)-0.70…9TP321S321000.08 2.000.0450.030 1.0017.0-19.09.0-12.0…0.10…5C-0.70…11TP321H S321090.04-0.10 2.000.0450.030 1.0017.0-19.09.0-12.0………4C-0.60…12TP347S347000.08 2.000.0450.030 1.0017.0-19.09.0-13.010xC-1.00……13TP347H S347090.04-0.10 2.000.0450.030 1.0017.0-19.09.0-13.0……8xC-1.00…… A、所有数值均为最大值除非指明范围或最小值。当本表中出现省略号（…）时没有要求，则用不着测定或做化学元素分析报告。 B、氮元素分析方法由供需双方协商确定； C、这些合金没有通用的级别标记。UNS编号可唯一识别这些合金； D、对于小外径或薄壁，或同时两者，当需要多道冷拔时，就级别TP304L,TP304LN,TP316L而言，其碳含量最大值需为0.040%； E T P316TP316H焊接管，镍含量范围10.0-14.0%。 第1页共4页

钢材化学成分元素知识大全

1、钢中酸溶铝指溶解在钢中单质铝，全铝应指酸溶铝和夹杂铝（氧化铝）。 2、水口堵塞的原因是什么，如何防止? 在浇注过程中，中间包水口和浸入式水口有时发生堵塞现象。堵塞的原因有两种，一是钢水温度低，水口未达到烘烤温度，钢水冷凝所致。二是因钢中高熔点(2052℃)的Al203沉积在水口内壁上，使钢流逐渐变小而造成水口堵塞。钢中的Al203主要来自脱氧产物，当钢中[Al]含量偏高时，[Al]与耐火材料中的Si02及空气中的氧或钢中[O]发生反应生成Al203。 为了防止水口堵塞，对含[Al]量不作要求的钢，应控制钢中全铝含量不大于0.006％。对铝含量有要求的钢，需对钢水进行钙处理，控制w[Ca]/w[A1]比值为0.1～0.15，使串簇状固体Al203转变成低熔点的12Ca0·7 Al203，这种铝酸钙熔点为1455℃，在浇注温度下为液态，可避免水口堵塞。如果钙的加入量过少，不足以将Al203转化为12CaO·7 Al203，钙的加入量过多，又会生成CaS(熔点2450℃)，不能消除水口堵塞。铝含量高(如w[Al]=0.045％)，硫含量也高(如w[S]>0.025％)的钢水难以避免水口堵塞。 提高钢水洁净度、减少钢水二次氧化，选择合适的水口材质，并向水口内壁和中间包塞棒吹氩等，都有利于避免水口的堵塞。 3、炼钢生产工艺中为了降低钢中的含氧量，常用铝、钡、钙、硅、锰等脱氧材料（或其复合合金）与氧发生反应成氧化物炉渣上浮到钢水上层而降低钢中的氧含量，其中铝是优良的脱氧剂，铝易与氧反应生成Al2O3（极少量氮化铝）,同时有部分单质铝溶入钢中，这部分单质铝可被酸溶解称为酸溶铝；而极少量的Al2O3也会滞留在钢中形成夹杂物，降低钢的性能，这部分Al2O3一般不易被酸溶解。单质铝和Al2O3的总含量成为全铝（含量）。 现在较新型的直读光谱仪入ARL4460、斯派克M8、M9型采用新型的激发电源和单脉冲火花测量技术，通过对单质铝和Al2O3激发时放电脉冲高度即发光强度的不同分别采集信号计算含量，可以测定单质铝和Al2O3。卖仪器的吹嘘能测酸溶铝和全铝，甚至在技术协议上保证测量精度是多少，实际安装调试仪器时他们的工程师也测不准。光谱仪测钢中全铝（大于0.0005%）基本上还可以，但测微量铝误差也比较大，对制样有较高的要求。 测定铝含量时,用化学分析是用酸溶解,单质铝可被酸溶解称为酸溶铝;铝氧化物不被溶解,称为酸不溶铝.我们平时测量的铝一般都是酸溶铝. 我们一般不要求进行这方面的测量,只有一些特钢才有这方面的要求.目前大部分光谱仪都是按一定的比例推算出来的.只有时间分解脉冲分布分析法技术才能测量出来. PDA技术是将激发时的每一个脉冲记录下来，并按时间顺序排列，将脉冲按高低频数制作分布图，依据数学统计的原则，选择正常激发信号来进行积分,能将样品中固溶元素和非固溶元素区分开。目前掌握这种测量方法的光谱仪厂家好象只有两家. 钢铁知识大全 钢铁知识大全(1) 钢材机械性能介绍 1.屈服点（σs） 钢材或试样在拉伸时，当应力超过弹性极限，即使应力不再增加，而钢材或试样仍继续发生明显的塑性变形，称此现象为屈服，而产生屈服现象时的最小应力值即为屈服点。 设Ps为屈服点s处的外力，Fo为试样断面积，则屈服点σs =Ps/Fo(MPa)，MPa称为兆帕等于N（牛顿）/mm2，（MPa=106Pa，Pa：帕斯卡=N/m2） 2.屈服强度（σ0.2） 有的金属材料的屈服点极不明显，在测量上有困难，因此为了衡量材料的屈服特性，规定产生永久残余塑性变形等于一定值（一般为原长度的0.2%）时的应力，称为条件屈服强度或简称屈服强度σ0.2 。 3.抗拉强度（σb） 材料在拉伸过程中，从开始到发生断裂时所达到的最大应力值。它表示钢材抵抗断裂的能力大小。与抗拉强度相应的还有抗压强度、抗弯强度等。 设Pb为材料被拉断前达到的最大拉力，Fo为试样截面面积，则抗拉强度σb= Pb/Fo （MPa）。 4.伸长率（δs） 材料在拉断后，其塑性伸长的长度与原试样长度的百分比叫伸长率或延伸率。

钢铁化学成分

钢号化学成分（%）机械性能（≥） C Si Mn P ≤S ≤ Cr Ni Mo Cu V σ b M Pa σ b M P a δ ％ Ψ ％ HB A K v J 碳钢铸件ZG200- 400 ≤ 0.2 ≤ 0.5 ≤ 0.8 0. 04 0. 04 ≤ 0.3 ≤ 0.30 ≤ 0.2 ≤ 0.30 ≤ 0.05 40 20 2 5 4 3 ZG230- 450 ≤ 0.3 ≤ 0.5 ≤ 0.9 0. 04 0. 04 ≤ 0.3 ≤ 0.30 ≤ 0.2 ≤ 0.30 ≤ 0.05 45 23 2 2 2 3 2 5 ZG270- 500 ≤ 0.4 ≤ 0.5 ≤ 0.9 0. 04 0. 04 ≤ 0.3 ≤ 0.30 ≤ 0.2 ≤ 0.30 ≤ 0.05 50 27 1 8 2 5 2 2 ZG310- 570 ≤ 0.5 ≤ 0.6 ≤ 0.9 0. 04 0. 04 ≤ 0.3 ≤ 0.30 ≤ 0.2 ≤ 0.30 ≤ 0.05 57 30 1 5 2 1 1 5 ZG340- 640 ≤ 0.6 ≤ 0.6 ≤ 0.9 0. 04 0. 04 ≤ 0.3 ≤ 0.30 ≤ 0.2 ≤ 0.30 ≤ 0.05 64 34 1 1 8 1 0 WCA≤ 0.2 5 ≤ 0.6 ≤ 0.7 0. 04 0. 04 5 ≤ 0.5 ≤ 0.50 ≤ 0.2 ≤ 0.30 ≤ 0.03 41 5 ～ 58 5 20 5 2 4 3 5 WCB≤ 0.3 ≤ 0.6 ≤ 1.0 0. 04 0. 04 5 ≤ 0.5 ≤ 0.50 ≤ 0.2 ≤ 0.30 ≤ 0.03 48 5 ～ 65 5 25 2 2 3 5 WCC≤ 0.2 5 ≤ 0.6 ≤ 1.2 0. 04 0. 04 5 ≤ 0.5 ≤ 0.50 ≤ 0.2 ≤ 0.30 ≤ 0.03 48 5 ～ 65 5 27 5 2 2 3 5 低合金钢ZG20Cr Mo 0.1 7～ 0.2 5 0.2 0～ 0.4 5 0.5 0～ 0.8 0. 03 0. 03 0.5 0～ 0.8 0.4 0～ 0.6 46 24 5 1 8 3 2 4 ZG35Cr Mo 0.3 0～ 0.3 7 0.3 0～ 0.5 0.5 0～ 0.8 0. 03 0. 03 0.8 0～ 1.2 0.2 0～ 0.3 74 ～ 88 51 1 2 2 7 ZG40Cr0.3 5～ 0.4 5 0.2 0～ 0.4 0.5 0～ 0.8 0. 03 0. 03 0.8 0～ 1.1 ≤ 0.1 5 63 34 5 1 8 2 6 ≥ 212 ZG15W1 Mo1V 0.1 4～ 0.2 0.1 5～ 0.3 0.4 0～ 0.7 0. 03 0. 03 1.2 0～ 1.7 1.0 ～ 1.2 53 9 34 3 2 3 5 ≥ 140

钢的化学成分

钢的化学成分 合金钢是在普通碳素钢基础上添加适量的一种或多种合金元素而构成的铁碳合金。 合金钢的主要合金元素有硅、锰、铬、镍、钼、钨、钒、钛、铌、锆、钴、铝、等。其中锰、铬、钨、钼为碳化物形成元素，其中一部分以原子状态进入固溶体中，另一部分形成置换式合金渗碳体；钒、钛、铌、锆等在钢中是强碳化物形成元素，只要有足够的碳，在适当条件下，就能形成各自的碳化物，当缺碳或在高温条件下，则以原子状态进入固溶体中；铝、铜、镍、钴、硅等是不形成碳化物元素，一般以原子状态存在于固溶体中。 钢的性能取决于钢的相组成，相的成分和结构，各种相在钢中所占的体积组分和彼此相对的分布状态。 目前在合金钢中常用的合金元素有：铬(Cr)，锰(Mn)，镍(Ni)，硅(Si)，硼(B)，钨(W)，钼(Mo)，钒(V)，钛(Ti)和稀土元素(Re)等。 铬是合金结构钢主加元素之一，在化学性能方面它不仅能提高金属耐腐蚀性能，也能提高抗氧化性能。当其含量达到13％时，能使钢的耐腐蚀能力显著提高，并增加钢的热强性。铬能提高钢的淬透性，显著提高钢的强度、硬度和耐磨性，但它使钢的塑性和韧性降低。

锰可提高钢的强度，增加锰含量对提高低温冲击韧性有好处。 镍钢铁性能有良好的作用。它能提高淬透性，使钢具有很高的强度，而又保持良好的塑性和韧性。镍能提高耐腐蚀性和低温冲击韧性。镍基合金具有更高的热强性能。镍被广泛应用于不锈耐酸钢和耐热钢.1、碳（C）：钢中含碳量增加，屈服点和抗拉强度升高，但塑性和冲击性降低，当碳量0.23%超过时，钢的焊接性能变坏，因此用于焊接的低合金结构钢，含碳量一般不超过0.20%。碳量高还会降低钢的耐大气腐蚀能力，在露天料场的高碳钢就易锈蚀；此外，碳能增加钢的冷脆性和时效敏感性。 2、硅（Si）：在炼钢过程中加硅作为还原剂和脱氧剂，所以镇静钢含有0.15－0.30%的硅。如果钢中含硅量超过0.50-0.60%,硅就算合金元素。硅能显著提高钢的弹性极限，屈服点和抗拉强度，故广泛用于作弹簧钢。在调质结构钢中加入1.0－1.2%的硅，强度可提高15－20%。硅和钼、钨、铬等结合，有提高抗腐蚀性和抗氧化的作用，可制造耐热钢。含硅1－4%的低碳钢，具有极高的导磁率，用于电器工业做矽钢片。硅量增加，会降低钢的焊接性能。 3、锰（Mn）：在炼钢过程中，锰是良好的脱氧剂和脱硫剂，一般钢中含锰0.30－0.50%。在碳素钢中加入0.70%以上时就算“锰钢”，较一般钢量的钢不但有足够的韧性，且有较高的强度和硬度，提高钢的淬性，改善

德国化学成分牌号与din系统的数字材料号对照表

QUALITY OUTLINE Following is a brief summary of available types of quality. Types not listed can be made available upon request. For further information, please feel free to contact us! Cold working steels

MATERIAL NO.DESCRIPTION/DIN AISI/SAE/ASTM OSSENBERG W 1WO 10 Extra1.1545C 105 W 1 W 11.1645C 105 W 2WO 10 Prima 10451.1730C 45 WWO 3 1.1740WO 5C 60 W 1.2056KP 690 Cr 3 NSZ1.2063145 Cr 6 L 3102 Cr 61.2067NSK D 3X 210 Cr 12ESC1.2080 420BPS 2X 42 Cr 131.2083 62 SiMnCr 4SPCR1.2101 KLS125 CrSi 51.2109 MNC105 MnCr 41.2127 5120BPS21 Mn Cr 51.2162 ESW1.2201X 165 CrV 12 1.2206Wo 120140 CrV 1 31 CrV 31.22081.2208 L 21.2210115 CrV 3CRV 1.224151 CrV 4OV 1.224259 CrV 4OVH 61 CrSiV 51.2243GBV 6 1.224838 SiCrV 6GBN 45 SiCrV 6GBV1.2249 85 CrMo 71.23041.2304 X 64 CrMo 14BSC1.2319 X 6 CrMo 4BPS 71.2341 27 CrMoV 6 121.23531.2353 S 750 CrMoV 13 141.23571.2357 1.23581.235860 CrMoV 18 5 A 2EPS 521.2363X 100 CrMoV 51 M 501.2369EPS 6981 MoCrV 42 16 1.2376BSC 2X 96 CrMoV 12 1.2378X220 CrVMo122ESV 2 D 21.2379ESMo 2 X155 CrVMo121 ESV 2 Sonder1.2378.10 74 CrW 1WO 4101.2410 UVW1.2419105 WCr 6 D 61.2436ESSX 210 CrW 12 115 W 81.24421.2442 X 130 W 5SS 5111.2453

各种化学成分对钢板的作用

各种化学成分对钢板的作用 1、碳（C）：钢中含碳量增加，屈服点和抗拉强度升高，但塑性和冲击性降低，当碳量0.23%超过时，钢的焊接性能变坏，因此用于焊接的低合金结构钢，含碳量一般不超过0.20% 。碳量高还会降低钢的耐大气腐蚀能力，在露天料场的高碳钢就 易锈蚀；此外，碳能增加钢的冷 脆性和时效敏感性。 2、硅（Si）：在炼钢过程中加硅作为还原剂和脱氧剂，所以镇静钢含有0.15－0.30%的硅。如果钢中含硅量超过0.50-0.60%,硅就算合金元素。硅能显著提 高钢的弹性极限，屈服点和抗拉强度，故广泛用于作弹簧钢。在调质结构钢中加入1.0－1.2%的硅，强度可提高15－20%。硅和钼、钨、铬等结合，有提高抗腐蚀性和抗氧化的作用，可制造耐热钢。含硅1－4%的低碳钢，具有极高的导磁率，用于电器工业做矽钢片。硅量增加，会降低钢的焊接性能。 3、锰（Mn）：在炼钢过程中，锰是良好的脱氧剂和脱硫剂，一般钢中含锰0.30－0.50%。在碳素钢中加入0.70%以上时就算“锰钢”，较一般钢量的钢不但有足够的 韧性，且有较高的 强度和硬度，提高钢的淬性，改善钢的热加工性能，如16Mn钢比A3屈服点高40%。含锰11－14%的钢有极高的 耐磨性，用于挖土机铲斗，球磨机衬板等。锰量增高，减弱钢的抗腐蚀能力，降低焊接性能。 4、磷（P）：在一般情况下，磷是钢中有害元素，增加钢的冷脆性，使焊接性能变坏，降低塑性，使冷弯性能变坏。因此通常要求钢中含磷量小于0.045%，优质钢要求更低些。 5、硫（S）：硫在通常情况下也是有害元素。使钢产生热脆性，降低钢的延展性和韧性，在锻造和轧制时造成裂纹。硫对焊接性能也不利，降低耐腐蚀性。所以通常要求硫含量小于0.055%，优质钢要求小于0.040%。在钢中加入0.08-0.20%的硫，可以改善切削加工性，通常称易切削钢。 6、铬（Cr）：在结构钢和工具钢中，铬能显著提高强度、硬度和耐磨性，但同时降低塑性和韧性。铬又能提高钢的抗氧化性和耐腐蚀性，因而是不锈钢，耐热钢的重要合金元素。 7、镍(Ni) ：镍能提高钢的强度，而又保持良好的塑性和韧性。镍对酸碱有较高的耐腐蚀能力，在高温下有防锈和耐热能力。但由于镍是较稀缺的资源，故应尽量采用其他合金元素代用镍铬钢。 8、钼(Mo)：钼能使钢的晶粒细化，提高淬透性和热强性能，在高温时保持足够的强度和抗蠕变能力(长期在高温下受到应力，发生变形，称蠕变)。结构钢中加入钼，能提高机械性能。还可以抑制合金钢由于火而引起的脆性。在工具钢中可提高红性。 9、钛(Ti)：钛是钢中强脱氧剂。它能使钢的内部组织致密，细化晶粒力；降低时效敏感性和冷脆性。改善焊接性能。在铬18镍9奥氏体不锈钢中加入适当的钛，可避免晶间腐蚀。 10、钒(V)：钒是钢的优良脱氧剂。钢中加0.5%的钒可细化组织晶粒，提高强度和韧性。钒与碳形成的碳化物，在高温高压下可提高抗氢腐蚀能力。 11、钨(W)：钨熔点高，比重大，是贵生的合金元素。钨与碳形成碳化钨有很高的硬度和耐磨性。在工具钢加钨，可显著提高红硬性和热强性，作切削工具及锻模具用。 12、铌(Nb)：铌能细化晶粒和降低钢的过热敏感性及回火脆性，提高强度，但塑性和韧性有所下降。在普通低合金钢中加铌，可提高抗大气腐蚀及高温下抗氢、氮、氨腐蚀能力。铌可改善焊接性能。在奥氏体不锈钢中加铌，可防止晶间腐蚀现象。 13、钴(Co) ：钴是稀有的贵重金属，多用于特殊钢和合金中，如热强钢和磁性材料。 14、铜(Cu)：武钢用大冶矿石所炼的钢，往往含有铜。铜能提高强度和韧性，特别是大气

化学成分对钢材性能的影响

列表整理化学成分对钢材性能的影响 钢是以铁和碳为主要成分的合金，虽然碳和其他元素所占比例甚少，但却左右着钢材的性能。 1、碳 碳时各种钢中的重要元素之一，在碳素结构钢中则是铁以外的最主要元素。碳是形成钢材强度的主要成分，随着含碳量的提高，钢的强度逐渐增高，而塑性和韧性下降，冷弯性能、焊接性能和抗锈性能等也变劣。碳素钢按碳含量区分，小于0.25%的为低碳钢，介于0.25%和0.6%之间的为中碳钢，大于0.6%的为高碳钢。含碳量超过0.3%时，钢材的抗拉强度很高，但却没有明显的屈服点，且塑性很小，含碳量超过0.2%时，钢材的焊接性能开始恶化。因此，规范推荐的钢材，含碳量均不超过0.22%，对于焊接结构则严格控制在0.2%以内。 2、硫 硫是有害元素，常以硫化铁形式夹杂于钢中。当温度达800~1000℃时，硫化铁会熔化使钢材变脆，因而在进行焊接或热加工时，有可能引发热裂纹，称为热脆。此外，硫还会降低钢材的冲击韧性、疲劳强度、抗锈蚀性能和焊接性能等。非金属硫化物夹杂经热轧加工后还会在厚钢板中形成局部分层现象，在采用焊接连接的节点中，沿板厚方向承受拉力时，会发生层状撕裂破坏。因而应严格限制钢

材中的含硫量，随着钢材牌号和质量等级的提高，含硫量的限制值由0.05%依次降至0.025%，厚度方向性能钢板（抗层状撕裂钢板）的含硫量更限制在0.01以下。 3、磷 磷可提高钢的强度和抗锈蚀能力，但却严重地降低钢的塑性、韧性、冷弯性能和焊接性能，特别是在温度较低时促使钢材变脆，称为冷脆。因此，磷的含量也要严格控制，随着钢材牌号和质量等级的提高，含磷量的限值由0.045%依次降至0.025%。但是当采用特殊的冶炼工艺时，磷可作为一种合金元素来制造含磷的低合金钢，此时其含量可达0.12%~0.13%。 4、锰 锰是有益元素，在普通碳素钢中，它是一种弱脱氧剂，可提高钢材强度，消除硫对钢的热脆影响，改善钢的冷脆倾向，同时不显著降低塑性和韧性。锰还是我国低合金钢的主要合金元素，其含量为0.8%~1.8%。但锰对焊接性能不利，因此含量也不宜过多。 5、硅 硅是有益元素，在普通碳素钢中，它是一种强脱氧剂，常与锰共同除氧，生产镇静钢。适量的硅，可以细化晶粒，提高钢的强度，而对塑性、韧性、冷弯性能和焊接性能无显著不良影响。硅的含量在一般镇静钢中为0.12%~0.3%，

钢铁中化学成分对钢材的作用

钢铁中化学成份对钢材的作用 1、碳（C）：钢中含碳量增加，屈服点和抗拉强度升高，但塑性和冲击性降低，当碳量0.23%超过时，钢的焊接性能变坏，因此用于焊接的低合金结构钢，含碳量一般不超过0.20%。碳量高还会降低钢的耐大气腐蚀能力，在露天料场的高碳钢就易锈蚀；此外，碳能增加钢的冷脆性和时效敏感性。 2、硅（Si）：在炼钢过程中加硅作为还原剂和脱氧剂，所以镇静钢含有0.15－0.30%的硅。如果钢中含硅量超过0.50-0.60%,硅就算合金元素。硅能显著提高钢的弹性极限，屈服点和抗拉强度，故广泛用于作弹簧钢。在调质结构钢中加入1.0－1.2%的硅，强度可提高15－20%。硅和钼、钨、铬等结合，有提高抗腐蚀性和抗氧化的作用，可制造耐热钢。含硅1－4%的低碳钢，具有极高的导磁率，用于电器工业做矽钢片。硅量增加，会降低钢的焊接性能。 3、锰（Mn）：在炼钢过程中，锰是良好的脱氧剂和脱硫剂，一般钢中含锰0.30－0.50%。在碳素钢中加入0.70%以上时就算“锰钢”，较一般钢量的钢不有足够的韧性，且有较高的强度和硬度，提高钢的淬性，改善钢的热加工性能，如16Mn钢比A3屈服点高40%。含锰11－14%的钢有极高的耐磨性，用于挖土机铲斗，球磨机衬板等。锰量增高，减弱钢的抗腐蚀能力，降低焊接性能。 4、磷（P）：在一般情况下，磷是钢中有害元素，增加钢的冷脆性，使焊接性能变坏，降低塑性，使冷弯性能变坏。因此通常要求钢中含磷量小于0.045%，优质钢要求更低些。 5、硫（S）：硫在通常情况下也是有害元素。使钢产生热脆性，降低钢的延展性和韧性，在锻造和轧制时造成裂纹。硫对焊接性能也不利，降低耐腐蚀性。所以通常要求硫含量小于0.055%，优质钢要求小于0.040%。在钢中加入

钢材化学成份及性能对照表新.docx

牌号 SPHC DD11 (StW22) SPCC St12(DCO1 ) DC04 St37-2G St44-3G St52-3G SS330 SS400 SS540 St33 S235JR （ST37-2) S355J0 (St52-3) SPHT1 SPHT2 SPHT3 SAPH310 SAPH370 SAPH400 SAPH440 QSTE340 QSTE380 QSTE420 QSTE460 QSTE500 B440QZR B480QZR Q195 Q215A Q215B Q235A Q235B Q235C Q235D SAE1008 SAE1010 SAE1020 SAE1022 10 20 45 37Mn5 40Cr Q345B (16Mn) Q345C (16MnAl) 25Mn 常用材料化学成份及机械性能对照表 化学成份（ %）机械性能 伸长率 C Si Mn S P Alt屈服强度 Mpa抗拉强度 Mpa（ % ） ≤ 0.15≤0.05≤0.60≤0.035≤ 0.035≥ 0.010------≥ 270≥27 ≤ 0.12≤0.05≤0.60≤0.035≤ 0.035≥ 0.010170 ～ 360≤ 440≥22 ≤ 0.15------≤0.60≤0.025≤ 0.10------------≥ 270≥25 ≤ 0.10------≤0.50≤0.025≤ 0.035≥ 0.015140 ～ 280≥ 270≥24 ≤ 0.08------≤0.40≤0.020≤ 0.025≥ 0.015130 ～ 210≥ 270≥34 ≤ 0.17------≤1.00≤0.030≤ 0.035≥ 0.015≥215360 ～ 510≥20 ≤ 0.20------≤1.30≤0.030≤ 0.035≥ 0.015≥245430 ～ 580≥18 ≤ 0.20------≤1.60≤0.030≤ 0.035≥ 0.015≥325510 ～ 680≥16 ≤ 0.15≤0.30≤0.95≤0.035≤ 0.035------≥205330 ～ 430≥26 ≤ 0.21≤0.30≤1.40≤0.035≤ 0.035------≥245400 ～ 510≥21 ≤ 0.30≤0.25≤1.60≤0.035≤ 0.035------≥400≥ 540≥16 ------------------≤0.040≤ 0.040------≥185310 ～ 540≥10 ≤ 0.17≤0.35≤1.40≤0.035≤ 0.035------≥235360 ～ 510≥17 ≤ 0.20≤0.55≤1.60≤0.030≤ 0.030------≥355510 ～ 680≥14 ≤ 0.10≤0.35≤0.50≤0.035≤ 0.035------------≥ 270≥30 ≤ 0.18≤0.35≤0.60≤0.035≤ 0.035------------≥ 340≥25 ≤ 0.25≤0.350.30 ～0.90≤0.035≤ 0.035------------≥ 410≥20 ≤ 0.10≤0.30≤0.50 ≤0.035≤ 0.035 ≥185≥ 310≥33 ≤0.75≥225≥ 370≥32 ≥ 0.010 ≤ 0.21≤0.30≤1.40≥255≥ 400≥31 ≤0.025≤ 0.030 ≤1.50≥305≥ 440≥29 ≤1.30≥340420 ～ 540≥19 ≤ 0.12≤0.50 ≤1.40 ≤0.025≤ 0.030 Nb ≤ 0.09≥380450 ～ 590≥18 ≤1.50V ≤0.20≥420480 ～ 620≥16 ≤1.60 Ti ≤ 0.15 ≥460520 ～ 670≥14 ≤1.70≥500550 ～ 700≥12 ≤ 0.12≤0.50≤1.30≤0.025≤ 0.030 ------ ≥320440 ～ 570≥15 ≤ 0.16≤0.50≤1.50≤0.035≤ 0.030≥355480 ～ 580≥21 ≤ 0.12≤0.30≤0.50≤0.040≤ 0.035------≥195315 ～ 430≥33 ≤ 0.15≤0.35≤1.20≤0.050≤ 0.045------≥215335 ～ 450≥31 ≤ 0.15≤0.35≤1.20≤0.050≤ 0.045------≥215335 ～ 450≥31 ≤ 0.22≤0.35≤1.40≤0.050≤ 0.045------≥235370 ～ 500≥26 ≤ 0.20≤0.35≤1.40≤0.045≤ 0.045------≥235370 ～ 500≥26 ≤ 0.17≤0.35≤1.40≤0.040≤ 0.040------≥235370 ～ 500≥26 ≤ 0.17≤0.35≤1.40≤0.035≤ 0.035------≥235370 ～ 500≥26 ≤ 0.10≤0.15≤0.50≤0.020≤ 0.020------ 180Mpa 热轧320Mpa 热轧28% 热轧 0.08 ～ ------0.30 ～0.60≤0.035≤ 0.035------ 0.13/300Mpa 冷拉/370Mpa 冷拉/20% 冷拉 0.18 ～ ------0.30 ～0.60≤0.030≤ 0.050------210Mpa 热轧380Mpa 热轧25% 热轧 0.23/350Mpa 冷拉/460Mpa 冷拉/15% 冷拉 0.18 ～ ≤0.150.70 ～1.00≤0.025≤ 0.030------ 0.23 ≥490≥ 36027% 0.17 ～ 0.07 ～0.35 ～0.65≤0.035≤ 0.035------------360 ～ 460≥20 0.130.37 0.17 ～0.17 ～0.35 ～0.65≤0.035≤ 0.035------------420 ～ 530≥24 0.230.37 0.42 ～0.17 ～ 0.50 ～0.80≤0.035≤ 0.035------------≥ 590≥14 0.450.37 0.34 ～0.20 ～ 1.25 ～1.50≤0.015≤ 0.020------------≥ 720≥18 0.390.35 0.37 ～0.17 ～0.50 ～0.80≤0.035≤ 0.035------------≥ 720≥14 0.440.37 ≤ 0.20≤0.50≤1.70≤0.035≤ 0.035------≥345470 ～ 630≥24 ≤ 0.20≤0.50≤1.70≤0.030≤ 0.030≥ 0.015≥345470 ～ 630≥24 0.22 ～0.17 ～ 0.70 ～1.00≤0.035≤ 0.035------------≥ 530≥20 0.290.37 标准 BQB302 BQB402 BQB403 BQB410 BQB303 BQB310 GB/T70 SAE J1397 GB/T69 9 兴澄标 准 GB/T307 7 GB/T159 1 GB/T69 9

常用钢Q235 ,Q345,Q245R的化学成分

常用钢Q235 ，Q345，Q245R的化学成分 Q235分A、B、C、D四级(GB700-88) Q235A级含C0.14~0.22% Mn0.30~0.65Si≤0.30S≤0.050P≤0.045 Q235B级含C0.12~0.20% Mn0.30~0.670Si≤0.30S≤0.045P≤0.045 Q235C级含C≤0.18% Mn0.35~0.80Si≤0.30S≤0.040P≤0.040 Q235D级含C≤0.17% Mn0.35~0.80Si≤0.35S≤0.040P≤0.035 参考资料：金属材料手册 Q345 是一种钢材的材质。它是低合金钢（C<0.2%)，广泛应用于桥梁、车辆、船舶、建筑、压力容器等。Q代表的是这种材质的屈服，后面的345，就是指这种材质的屈服值，在345左右。并会随着材质的厚度的增加而使其屈服值减小。 化学成分 Q345A：C≤0.20，Mn 1.0~1.6，Si≤0.55，P≤0.045，S≤0.045，V 0.02~0.15； Q345B：C≤0.20，Mn 1.0~1.6，Si≤0.55，P≤0.040，S≤0.040，V 0.02~0.15； Q345C：C≤0.20，Mn 1.0~1.6，Si≤0.55，P≤0.035，S≤0.035，V 0.02~0.15，Al≥0.015； Q345D：C≤0.20，Mn 1.0~1.6，Si≤0.55，P≤0.030，S≤0.030，V 0.02~0.15，Al≥0.015； Q345E：C≤0.20，Mn 1.0~1.6，Si≤0.55，P≤0.025，S≤0.025，V

0.02~0.15，Al≥0.015 Q245R的成分 化学成分：C：≤0.20，Si：≤0.35，Mn：0.50—1.00，P：≤0.025，S：≤0.015，Alt：≥0.020.

常用钢材化学成分

常用钢铁材料化学成份.力学性能 一、《蜗炉用钢板》GB 723--1997 20g C≤0.20 Si 0.15~0.30 Mn 0.50~0.90 P≤0.035 S≤0.035 (试样,横向) σb 400~520 σs≥225 δ5≥25 A kv≥27 J A ku≥29 J·cm-2 d＝1.5a 16Mng C≤0.20 Si 0.20~0.55 Mn 1.20~1.60 P≤0.035 S≤0.030 (试样,横向) σb 490~630 σs≥325 δ5≥19(a＞16~25) A kv≥27 J A ku≥29 J·cm-2 d＝3a（180°）19Mng C 0.15~0.22 Si 0.30~0.60 Mn 1.00~1.60 P≤0.03 S≤0.025 σb 510~650 σs≥345δ5≥20(a＞16~40) A kv≥31 J d＝3a（180°试样,横向) 二、《压力容器用钢板》GB 6654--1996 20R C≤0.22 Si 0.15~0.30 Mn 0.35~0.90 P≤0.035 S≤0.030 σb 400~520 σs≥235 δ5≥25(a＞16~36) A kv≥31 J（20°）d＝2a（180°试样,横向) 16MnR C≤0.20 Si 0.20~0.55 Mn 1.20~1.60 P≤0.035 S≤0.030 σb 490~620 σs≥325 δ5≥21(a＞16~36) A kv≥31 J（20°）d＝2a（180°） 15MnVR C≤0.18 Si 0.20~0.55 Mn 1.20~1.60 V 0.04~0.12 P≤0.035 S≤0.030 σb 510~645 σs≥370 δ5≥19(a＞16~36) A kv≥31 J（20°）d＝2a（180°试样,横向) 15CrMoR C 0.12~0.18 Si 0.15~0.40 Mn 0.40~0.70 Mo 0.45~0.60 Cr 0.80~1.20 P≤0.030 S≤0.030 (试样,横向) σb 450~590 σs≥295 δ5≥19(a＞6~60) A kv≥31 J（20°）d＝2a（180°） 三、《碳素结构钢》GB /T700--1988 Q235-A C 0.14~0.22 Mn 0.30~0.65 P≤0.045 S≤0.050 (试样,纵向) σb 375~500 σs≥235 δ5≥26(a＜16) σb 375~500 σs≥225 δ5≥25(a＞16~40) σb 375~500 σs≥215 δ5≥24(a＞40~60) A kv≥无d＝a（180°） Q235-B C 0.12~0.20 Si ≤0.30 Mn 0.30~0.70 P≤0.045 S≤0.045 (试样,纵向) σb 375~500 σs≥235 δ5≥26(a＜16) σb 375~500 σs≥225 δ5≥25(a＞16~40) σb 375~500 σs≥215 δ5≥24(a＞40~60) A kv≥27 J（20°）d＝a（180°）Q235-C C ≤0.18 P≤0.040 S≤0.040 Si ≤0.30 Mn 0.35~0.80 σb 375~500 σs≥235 δ5≥26(a＜16) σb 375~500 σs≥225 δ5≥25(a＞16~40) σb 375~500 σs≥215 δ5≥24(a＞40~60) A kv≥27 J（0°试样,横向）d＝1.5a（180°） 四、《伏质碳素结构钢》GB /T699--1999 15# C 0.12~0.18 Si 0.17~0.37 Mn 0.35~0.65 P≤0.035 S≤0.035 σb≥375 σs≥225 δ5≥26 (试样,φ25) A kU≥27 J ψ≥55HBS≤143 20# C 0.17~0.24 Si 0.17~0.37 Mn 0.35~0.65 P≤0.035 S≤0.035 σb 340~470 σs≥215 δ5≥24 (试样,≤φ100) σb 320~470 σs≥205 δ5≥23 (试样,100~250) σb 320~470 σs≥195 δ5≥22 (试样,250~500) ψ≥53A kU≥54 J HBS 105~156 25# C 0.22~0.29 Si 0.17~0.37 Mn 0.50~0.80 P≤0.035 S≤0.035 σb≥450σs≥275 δ5≥23(试样,φ25) ψ≥50 A kU≥71 J HBS ≤170 JB /T6397--1992 σb 410~540 σs≥235 δ5≥20(试样,≤φ100) ψ≥50A kU≥49 J HBS 120~155 σb 390~520 σs≥225 δ5≥19(试样,100~250) ψ≥48A kU≥39 J HBS 120~155 σb 390~520 σs≥215 δ5≥18(试样,250~500) ψ≥40A kU≥39J HBS 120~155 35# C 0.32~0.39 Si 0.17~0.37 Mn 0.50~0.80 P≤0.035 S≤0.035 ⑴σb≥530 σs≥315 δ5≥20(试样,φ25) ψ≥45 A kU≥55 J HBS ≤197 JB /T6397--1992 ⑵σ b 490~630 σs≥255 δ5≥18 (试样,≤100) ψ≥43A kU≥34 J HBS 140~172 (正火) ⑶σ b 450~590 σs≥240 δ5≥17(试样,100~250) ψ≥40A kU≥29 J HBS 140~172 (正火) ⑷σ b 450~590 σs≥220 δ5≥16(试样,250~500) ψ≥27A kU≥29 J HBS 140~172 (正火) ⑸σ b 550~700 σs≥320 δ5≥20 (试样,40~100) ψ≥45A kU≥40 J HBS 196~241 (调质) ⑹σb 490~640 σs≥295 δ5≥22 (试样,100~250) ψ≥40 A kU≥40 J HBS 189~229 (调质) ⑺σb 490~640 σs≥275 δ5≥21 (试样,250~500) ψ≥无A kU≥38 J HBS 163~219 (调质)