可控制备磁性四氧化三铁-金纳米复合颗粒及其催化性能研究

第33卷 第2期

无 机 材 料 学 报 Vol. 33

No. 2 2018年2月

Journal of Inorganic Materials Feb., 2018

收稿日期: 2017-08-14; 收到修改稿日期: 2017-10-31

作者简介: 李永生(1972–), 男, 教授. E-mail: ysli@https://www.wendangku.net/doc/cf4716940.html,

文章编号: 1000-324X(2018)02-0221-08 DOI: 10.15541/jim20170394

可控制备磁性四氧化三铁-金纳米复合颗粒

及其催化性能研究

李永生, 陈 玲

(华东理工大学 材料科学与工程学院, 上海 200237)

摘 要: 随着纳米催化剂的不断发展, 基于纳米金的多功能复合材料以其高效的催化性能而受到广泛关注。本研究采用简单可控的原位还原法, 制备了一种粒径均一、分散性良好、可快速磁分离且具有高催化活性与催化稳定性的磁性四氧化三铁-金纳米复合颗粒。首先用有机硅源-巯丙基三乙氧基硅烷(MPTES)水解得到的有机硅层来包覆粒径约100 nm 的亲水四氧化三铁(Fe 3O 4)纳米颗粒, 再通过有机硅层表面的巯基来锚定原位还原生成的尺寸可控的金纳米颗粒(2 nm 或6 nm), 得到内核为四氧化三铁、壳层为金纳米颗粒均匀修饰有机硅层的磁性氧化硅复合颗粒。利用透射电子显微镜(TEM)、动态光散射仪(DLS)和振动样品磁强计(VSM)等对所合成材料进行系统表征, 结果表明: 合成的磁性氧化硅复合颗粒核壳结构明显, 分散性良好, 粒径约为150 nm; 饱和磁强度为32.1 A ·m 2/kg, 具有良好的超顺磁特性。将其应用于4-硝基苯酚的催化还原, 转化频率(TOF)值高达70 s -1, 远高于文献报道值, 五次循环反应后的转化率依然高达98%, 证实其具备高催化活性及良好的循环催化性能。

关 键 词: 原位还原; 磁性四氧化三铁-金纳米复合颗粒; 超顺磁性; 高催化活性; 循环性能

中图分类号: TQ174 文献标识码: A

Controlled Synthesis of Gold-based Magnetic Nanocomposites and

Their Catalytic Performance

LI Yong-Sheng, CHEN Ling

(School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237, China)

Abstract: With the rapid development of nanocatalysts, gold-based nanocomposites have attracted more and more attention due to their excellent catalytic capability. In this study, a novel kind of gold-based magnetic nanocomposite with uniform size, high dispersity, magnetic separability, highly catalytic efficiency, and stability was facilely fabri-cated via a controllable in-situ reducing approach. Firstly, magnetic nanocomposites were synthesized through coating 100 nm-sized hydrophobic Fe 3O 4 nanoparticles with organosilica shell formed by the hydrolysis of mercaptopropyl-triethoxysilane (MPTES). Then, size-controllable gold nanoparticles (2 nm or 6 nm) formed via in situ reduction was anchored onto the organosilica shell via Au-S covalent bonding, so that gold-based magnetic nanocomposites consisted of Fe 3O 4 nanoparticles as core and gold nanoparticles decorated organosilica as shell were obtained. Various tech-niques, such as Transmission Electron Microscope (TEM), Dynamic Light Scattering (DLS) and Vibrating Sample Magnetometer (VSM) were employed to characterize the as-synthesized samples. It is demonstrated that the as-prepared nanocomposite is highly-dispersed, core-shell structured and superparamagnetic with diameter of ~150 nm. The saturation magnetization was measured to be 32.1 Am 2/kg. Furthermore, the turnover frequency (TOF) of MCN-Au (2 nm) is calculated to be 70 s -1 towards the catalytic reduction of 4-nitrophenol (4-NP) to 4-aminophenol 万方数据